Superconducting nanowire single-photon detectors (SNSPDs) at a wavelength of 532 nm were designed and fabricated aiming to satellite laser ranging (SLR) applications. The NbN SNSPDs were fabricated on one-dimensional photonic crystals with a sensitive-area diameter of 42 μm. The devices were coupled with multimode fiber (ϕ = 50 μm) and exhibited a maximum system detection efficiency of 75% at an extremely low dark count rate of <0.1 Hz. An SLR experiment using an SNSPD at a wavelength of 532 nm was successfully demonstrated. The results showed a depth ranging with a precision of ~8.0 mm for the target satellite LARES, which is ~3,000 km away from the ground ranging station at the Sheshan Observatory.
Superconducting nanowire single-photon detectors (SNSPDs) at a wavelength of 532 nm were designed and fabricated aiming to satellite laser ranging (SLR) applications. The NbN SNSPDs were fabricated on one-dimensional photonic crystals with a sensitive-area diameter of 42 μm. The devices were coupled with multimode fiber (ϕ = 50 μm) and exhibited a maximum system detection efficiency of 75% at an extremely low dark count rate of <0.1 Hz. An SLR experiment using an SNSPD at a wavelength of 532 nm was successfully demonstrated. The results showed a depth ranging with a precision of ~8.0 mm for the target satellite LARES, which is ~3,000 km away from the ground ranging station at the Sheshan Observatory.
Satellite-ground quantum communication requires single-photon detectors of 850-nm wavelength with both high detection efficiency and large sensitive area. We developed superconducting nanowire single-photon detectors (SNSPDs) on one-dimensional photonic crystals, which acted as optical cavities to enhance the optical absorption, with a sensitive-area diameter of 50 μm. The fabricated multimode fiber coupled NbN SNSPDs exhibited a maximum system detection efficiency (DE) of up to 82% and a DE of 78% at a dark count rate of 100 Hz at 850-nm wavelength as well as a system jitter of 105 ps.
Superconducting nanowire single photon detectors (SNSPDs) have demonstrated advantages over traditional detectors in many fields [1]. Most fiber-coupled SNSPDs are coupled to single mode fibers, limiting their usability for applications where large surface area detectors are needed, for example fluorescence detection and satellite-based quantum communication [2][3]. Other important requirements for many applications are broadband detection efficiency, and low timing jitter [4]. So far, the increased meander length of multimode detectors, and the therefore increased kinetic inductance and number of imperfections due to film inhomogeneities have limited the timing jitter [5]. Moreover, combining low timing jitter with high detection efficiency and low dark count rate in one device is challenging due to the tradeoffs between different properties of SNSPDs [6]. In this paper, we achieved high efficiency and strong saturation over a broad wavelength range with a low timing jitter of 16.99 ps while maintaining a low dark count rate of < 0.2 Hz for an SNSPD coupled to a 50 µm core multimode fiber. To enhance the broadband absorption from 405 nm to 830 nm, detectors were fabricated on an optimized SiO2 cavity and Aluminum mirror. The geometry of the nanowire was also tuned to reach a good internal saturation of efficiency over the visible/NIR range but also to carry high current to get a large signal. Furthermore, a cryogenic readout amplifier was optimized to improve the signal to noise ratio and thus lead to high time resolution. Our devices can be readily used to enable higher resolution and faster quantum optics, bio-imaging, laser ranging and other optical experiments.
We develop single-photon detectors comprising single-mode fiber-coupled superconducting nanowires, with high system detection efficiencies at a wavelength of 940 nm. The detector comprises a 6.5-nm-thick, 110-nm-wide NbN nanowire meander fabricated onto a Si substrate with a distributed Bragg reflector for enhancing the optical absorptance. We demonstrate that, via the design of a low filling factor (1/3) and active area (Φ = 10 μm), the system reaches a detection efficiency of ∼60% with a dark count rate of 10 Hz, a recovery time <12 ns, and a timing jitter of ∼50 ps.
Single photon detection advanced rapidly in the last decade. The superconducting nanowire single-photon detector (SNSPD) is an emerging technology, which offers low dark count rates, broadband sensitivity from visible to mid-infrared wavelengths and very high quantum efficiency. All these features are appealing for future emerging applications in remote gas sensing, quantum key distribution and quantum information processing. By enclosing the detector in an optical cavity, tuned to the operating wavelength, the total system detection of the SNSPD is improved. Based on the cavity design, the detector absorption is boosted at the desired experimental wavelength. Devices have been fabricated and tested, in this thesis, with enhanced detection efficiency at near-infrared, infrared and mid-infrared wavelengths. NbTiN detectors fabricated on Ta2O5 / SiO2 distributed Bragg reflectors (DBR) for front-side coupling exhibit a system detection efficiency of ≈ 90% at λ = 940 nm for the best device measured. SNSPDs were also fabricated in NbTiN on metallic mirrors for back-side coupling for 1550 and 2333 nm experimental wavelengths. The first design exhibited a system detection efficiency of ≈ 84.5%, at λ = 1550 nm for the best device measured. The second exhibited low system detection efficiency since the device suffered from unexpectedly high dark count rate mainly due to blackbody radiation at 2.2 K. However, it was possible to measure the timing jitter of this device at 350 mK indicating a FWHM of 84 ps. Another technique to improve the total system detection efficiency of the SNSPD, is by fabricating a hairpin-shaped nanowire atop a single mode waveguide. In this design, photons travel through the waveguide and via evanescent coupling are absorbed in the nanowire. These SNSPD devices have been designed to thread along single mode Si ridge waveguides using a hairpin-shaped nanowire structure, which offers enhanced coupling and absorption efficiency via evanescent coupling. These ultra-thin superconducting MoSi detectors are precisely patterned on top of a single mode Si waveguide (600 nm) with alignment error less than 40 nm. Low temperature electrical and nano-optical characterization was carried out using a two-stage pulse tube (PT) coldhead, using an additional 4He / 3He sorption pump, low vibration characterization of SNSPD devices at 350 mK was carried out. Characterised devices exhibit low dark count rate <5 counts per second and timing jitter of ≈ 83 ps full width half maximum (FWHM) at wavelength (λ) = 1550 nm and at critical current ≈ 30 µA.
We demonstrate superconducting nanowire single photon detector (SNSPD) for the wavelength at around 2 μm. The linewidth of the NbN nanowire is squeezed to 56 nm to increase the intrinsic response efficiencies at longer wavelengths such as 2 μm. Serially connecting avalanche architecture is applied to increase the signal-to-noise ratio (SNR) of the response signal. Further, the optical cavity is optimized to improve the absorption of the device. A silica single-mode fiber is adopted to introduce photons to the SNSPD at a temperature of 2.25 K using a Gifford-McMahon cryocooler. The SNSPD exhibits detection efficiencies of 58%, 67%, and 63% at wavelengths of 1550, 1700, and 2000 nm, respectively, with dark count rate of ~12 kcps, which is reduced to 2 cps when the attached fiber pigtail is all placed inside the 40-K cryostat. The detection efficiency at 2000 nm is 2.5 times greater than that of the best previously developed detector with an efficiency of 25%. Our SNSPD is promising for practical applications in molecular science and earth meteorology.
We have developed a practical superconducting nanowire single photon detector (SNSPD) system with our superconducting thin films and devices fabrication, optical coupling packaging, and cryogenic technology. The SNSPD devices were fabricated from high-quality niobium nitride (NbN) ultra-thin films that were epitaxially grown on single-crystal MgO substrates, and optical cavity structure were applied for improvement of photo absorption efficiency. The SNSPD system was developed based on a compact Gifford-McMahon (GM) cryocooler, in which SNSPD can operate continuously at temperature of 2.9 K +/- 10 mK with low power consumption without any liquid cryogens. The system detection efficiencies at 1550 nm wavelength (at a 100 Hz dark count rate) were found to be 2.6% for device without optical cavity and 21% for device with optical cavity. The response speed of devices showed maximally 200 MHz with 5 × 5 mm square device, and timing jitter of 100 ps full width at a half maximum (FWHM) was observed.