Abstract Thin films provide nanoscale confinement together with compatibility with photonic and microwave architectures, making them ideal candidates for chip‐scale quantum devices. In this work, we propose a thin film fabrication approach yielding the epitaxial growth of Eu 3+ doped Y 2 O 3 on silicon. We combine two of the most prominent thin film deposition techniques: chemical vapor deposition (CVD) and molecular beam epitaxy (MBE). We report sub‐megahertz optical homogeneous linewidths up to 8 K for the Eu 3+ dopants in the film, and lowest value of 270 kHz. This result constitutes a ten‐fold improvement with respect to previous reports on the same material, opening promising perspectives for the development of scalable and compact quantum devices containing rare‐earth ions.
Abstract Thin films provide nanoscale confinement together with compatibility with photonic and microwave architectures, making them ideal candidates for chip‐scale quantum devices. In this work, we propose a thin film fabrication approach yielding the epitaxial growth of Eu 3+ doped Y 2 O 3 on silicon. We combine two of the most prominent thin film deposition techniques: chemical vapor deposition (CVD) and molecular beam epitaxy (MBE). We report sub‐megahertz optical homogeneous linewidths up to 8 K for the Eu 3+ dopants in the film, and lowest value of 270 kHz. This result constitutes a ten‐fold improvement with respect to previous reports on the same material, opening promising perspectives for the development of scalable and compact quantum devices containing rare‐earth ions.
Rare earth ions hosted in solids are good candidates for quantum technologies due to their chemical stability and optical and spin transitions exhibiting long coherence lifetimes. While bulk oxide crystals are usually the preferred host material, the development of a scalable silicon-compatible thin film platform would be desirable. In this paper, we report on the growth of Y2(1−x)Eu2xO3 thin films on silicon in the full range of Eu3+ concentration by direct liquid injection chemical vapor deposition (CVD). Our sub-micrometer polycrystalline films with a strong-(111) texture were grown for all compositions into the bixbyite cubic phase. The variation of growth rates with temperature and flow indicated that deposition occurred through a mass-transport controlled regime. Optical assessment of the Eu-doped thin films showed inhomogeneous linewidths as narrow as 50 GHz and fluorescence lifetimes of 1 ms for the lowest concentrations. Finally, a spectral hole was successfully burned in a 200 nm-thin film with a 2% Eu doping leading to a homogeneous linewidth of 11 MHz. These values are still below those reported for bulk single crystals indicating that additional decoherence mechanisms exist in such nanometric films, which might be alleviated by further improvement of the crystalline quality. Nevertheless, these results pave the way to the use of CVD-grown Eu:Y2O3 thin films as a platform for integrated quantum devices.
The obtention of quantum-grade rare-earth-doped oxide thin films that can be integrated with optical cavities and microwave resonators is of great interest for the development of scalable quantum devices. Among the different growth methods, chemical vapor deposition (CVD) offers high flexibility and has demonstrated the ability to produce oxide films hosting rare-earth ions with narrow linewidths. However, growing epitaxial films directly on silicon is challenging by CVD due to a native amorphous oxide layer formation at the interface. In this manuscript, we investigate the CVD growth of erbium-doped yttrium oxide (Er:Y2O3) thin films on different substrates, including silicon, sapphire, quartz, or yttria stabilized zirconia (YSZ). Alternatively, growth was also attempted on an epitaxial Y2O3 template layer on Si (111) prepared by molecular beam epitaxy (MBE) in order to circumvent the issue of the amorphous interlayer. We found that the substrate impacts the film morphology and the crystalline orientations, with different textures observed for the CVD film on the MBE-oxide/Si template (111) and epitaxial growth on YSZ (001). In terms of optical properties, Er3+ ions exhibit visible and IR emission features that are comparable for all samples, indicating a high-quality local crystalline environment regardless of the substrate. Our approach opens interesting prospects to integrate such films into scalable devices for optical quantum technologies.
The obtention of quantum-grade rare-earth doped oxide thin films that can be integrated with optical cavities and microwave resonators is of great interest for the development of scalable quantum devices. Among the different growth methods, Chemical Vapour Deposition (CVD) offers high flexibility and has demonstrated the ability to produce oxide films hosting rare-earth ions with narrow linewidths. However, growing epitaxial films directly on silicon is challenging by CVD due to a native amorphous oxide layer formation at the interface. In this manuscript, we investigate the CVD growth of erbium-doped yttrium oxide (Er:Y2O3) thin films on different substrates, including silicon, sapphire, quartz or yttria stabilized zirconia (YSZ). Alternatively, growth was also attempted on an epitaxial Y2O3 template layer on Si (111) prepared by molecular beam epitaxy (MBE) in order to circumvent the issue of the amorphous interlayer. We found that the substrate impacts the film morphology and the crystalline orientations, with different textures observed for the CVD film on the MBE-oxide/Si template (111) and epitaxial growth on YSZ (001). In terms of optical properties, Er3+ ions exhibit visible and IR emission features that are comparable for all samples, indicating a high-quality local crystalline environment regardless of the substrate. Our approach opens interesting prospects to integrate such films into scalable devices for optical quantum technologies.
Rare-earth ion dopants in solid-state hosts are ideal candidates for quantum communication technologies, such as quantum memories, due to the intrinsic spin–photon interface of the rare-earth ion combined with the integration methods available in the solid state. Erbium-doped cerium oxide (Er:CeO2) is a particularly promising host material platform for such a quantum memory, as it combines the telecom-wavelength (∼1.5μm) 4f–4f transition of erbium, a predicted long electron spin coherence time when embedded in CeO2, and a small lattice mismatch with silicon. In this work, we report on the epitaxial growth of Er:CeO2 thin films on silicon using molecular beam epitaxy, with controlled erbium concentration between 2 and 130 parts per million (ppm). We carry out a detailed microstructural study to verify the CeO2 host structure and characterize the spin and optical properties of the embedded Er3+ ions as a function of doping density. In as-grown Er:CeO2 in the 2–3 ppm regime, we identify an EPR linewidth of 245(1) MHz, an optical inhomogeneous linewidth of 9.5(2) GHz, an optical excited state lifetime of 3.5(1) ms, and a spectral diffusion-limited homogeneous linewidth as narrow as 4.8(3) MHz. We test the annealing of Er:CeO2 films up to 900 °C, which yields narrowing of the inhomogeneous linewidth by 20% and extension of the excited state lifetime by 40%.
The development of quantum technologies is generating great interest, as they promise major breakthroughs in computational power, measurement sensitivity and precision, as well as communication security, with potential applications acrossdiverse fields such as healthcare or electronics. In this context, rare-earth-doped oxide thin films represent a competitivesolid-state quantum platform for light–matter interactions. This is due to the ability of rare-earth ions to exhibit quantumcoherent states with long coherence times, combined with the nanometric thickness of the films, which makes them compatible with diverse photonic architectures. Chemical vapor deposition (CVD) offers a fast and cost-effective techniquefor producing thin films with good crystalline quality. However, compared to bulk crystals and ceramics, their propertiesare often degraded, likely due to surface proximity, a higher density of point defects, and strain. The use of epitaxial thinfilms, with a reduced defect density, is expected to lead to improved coherence times. The aim of this PhD project istherefore to obtain epitaxial CVD thin films and to enhance their crystalline properties in order to achieve light–matterinterfaces with long coherence times. Thin films were grown on various substrates, including silicon, oxides (quartz, sapphire, yttria-stabilized zirconia, YSZ), and hybrid substrates with a first layer deposited by molecular beam epitaxy (MBE).In parallel, the influence of post-deposition annealing treatments on the crystalline and optical properties of the films wasinvestigated. Epitaxy on hybrid substrates and YSZ was confirmed, with optical coherence times (T2) of 1.1 µs and 0.8µs, respectively, more than twenty times longer than those measured in polycrystalline films of equivalent composition.This epitaxial architecture paves the way for nanostructuring and integration into photonic devices such as resonators andwaveguides.
Abstract Rare earth doped crystals show, at low temperatures, extremely narrow optical homogeneous linewidths, as well as long spin coherence lifetimes, a unique combination in the solid state. This makes these materials attractive for optical quantum technologies like quantum communication and processing. Most of the results in this field have so far used bulk crystals because of their exceptional spectroscopic properties. Crystalline thin films can combine these properties with the possibilities offered by integration in photonic circuits in terms of compactness, stability, energy efficiency, and scalability. In this review, recent results on different platforms containing rare earth ions and targeting quantum technologies, including lithium niobate and silicon films, and oxide films deposited on Si, are summarized. Current approaches for obtaining thin films and devices are described, together with RE spectroscopic properties and applications to quantum technologies. The opportunities and challenges offered or faced by the different platforms are also discussed.