This study investigates the defects, imperfections, and variations in superconducting Nb thin films deposited on sapphire substrates. Two samples, W114 and W118, were fabricated using DC Magnetron Sputtering and Electron Cyclotron Resonance (ECR), respectively. Each sample was analyzed at five distinct spots to compare elemental homogeneity and thickness variations. Scanning Electron Microscopy (SEM) was employed to examine surface morphology, while Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS) provided elemental and chemical state analyses. SEM revealed distinct structures in W114 and a uniform surface in W118. EDS showed higher aluminum and oxygen signals in W118, indicating a thicker film. XPS detected a higher Nb₂O₅ signal in W118, attributed to a thicker oxygen layer. These findings highlight the critical role of precise material characterization in advancing quantum computing technologies.
This study investigates the defects, imperfections, and variations in superconducting Nb thin films deposited on sapphire substrates. Two samples, W114 and W118, were fabricated using DC Magnetron Sputtering and Electron Cyclotron Resonance (ECR), respectively. Each sample was analyzed at five distinct spots to compare elemental homogeneity and thickness variations. Scanning Electron Microscopy (SEM) was employed to examine surface morphology, while Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS) provided elemental and chemical state analyses. SEM revealed distinct structures in W114 and a uniform surface in W118. EDS showed higher aluminum and oxygen signals in W118, indicating a thicker film. XPS detected a higher Nb₂O₅ signal in W118, attributed to a thicker oxygen layer. These findings highlight the critical role of precise material characterization in advancing quantum computing technologies.
This study investigates the defects, imperfections, and variations in Nb thin films deposited on sapphire substrates. Two samples, W114 and W118, were fabricated using DC Magnetron Sputtering and Electron Cyclotron Resonance (ECR), respectively. Each sample was analyzed at five distinct spots to compare elemental homogeneity and variations in oxide layers. Scanning Electron Microscopy (SEM) was employed to examine surface morphology, while Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS) provided elemental and chemical state analyses. SEM revealed distinct structures in W114 and a uniform surface in W118. EDS showed higher aluminum signals in W118, indicating a thinner film in comparison to W114. XPS detected a higher Nb₂O₅ signal in W118, in comparison to W114, which can be attributed to the presence of a thicker Nb₂O₅ layer in W118. These findings highlight the critical role of precise material characterization in advancing quantum computing technologies.
Superconducting quantum circuits (SQC) are one of the most promising hardware platforms for quantum computing, yet their performance is currently limited by the presence of various structural defects inside the circuit’s structure. Despite impressive progress in the past decade, a precise understanding of the origin of these defects from various fabrication processes and their impact on coherence is still lacking. In this study, we performed a comprehensive investigation on the microstructure, superconductivity, and resonator quality factor of Nb films deposited by high-power impulse magnetron sputtering (HiPIMS) and direct current (DC) magnetron sputtering. A suite of characterization techniques, including electron microscopy with spectroscopy, secondary ion mass spectrometry, magneto-optical microscopy, and pump-probe reflectivity spectroscopy is used. We reveal that niobium (Nb) resonators fabricated using HiPIMS exhibit a smaller average grain size, thicker surface oxide with larger thickness variations (rougher surface), and a thicker amorphous Nb/Si interface layer compared to samples deposited by DC sputtering. We identified that the amorphous Nb oxides (mainly located at the Nb surface and along the grain boundaries) and Nb-Si amorphous layers (at the Nb/Si interface) are major and potential sources of two-level system (TLS), while off-stochiometric oxides and suboxides of Nb close to the surface, crystalline defects (i.e., dislocations at GB, point defects introduced during deposition) are main contributors of non-TLS sources. Our findings clarify the relationship between different defects and coherence loss mechanisms, highlighting the importance of material microstructure control on performance optimization in SQC.
ABSTRACT Niobium (Nb) films have emerged as a crucial material in the development of superconducting qubits, which are key components in quantum computing technology. This review provides a comprehensive examination of Nb films from a materials perspective, focusing on their intrinsic properties, fabrication methods/techniques, and their influence on qubit performance, particularly through surface and interface driven loss mechanisms. We discuss the key material properties that are essential for qubit operation. Various deposition techniques for Nb thin films, such as sputtering, evaporation, molecular beam epitaxy, and atomic layer deposition, are explored, alongside their impact on film quality, uniformity, and qubit performance. Additionally, the influence of surface roughness, thin‐film thickness, and substrate materials on quantum coherence is analyzed. Challenges such as defects and material degradation in Nb films are reviewed, along with strategies to mitigate these issues. Finally, we present the latest advancements and future directions in Nb film research, including potential improvements to enhance qubit coherence and scalability for large‐scale quantum computing systems. Ultimately, a deeper understanding of surface and interface phenomena is essential for pushing the limits of qubit performance and realizing next‐generation quantum technologies.
Superconducting qubits are among the most advanced platforms for quantum information, offering potential scalability and compatibility with standard device fabrication techniques [1-5]. Among the materials investigated for superconducting qubits, Tantalum (Ta) has emerged as a compelling candidate due to its self-terminating stoichiometric surface oxide and chemical resistance to harsh post-fabrication processes. Efforts to mitigate surface loss by treating the surface oxides and utilizing high-resistivity silicon substrates have led to Ta-based qubits with lifetime and coherence times exceeding 1 ms [3]. Guided by these successes in reducing dielectric loss in Ta-based devices, we are interested in exploring material engineering approaches that enhance the superconducting gap. Alloying Ta with another element to enhance the superconducting performance expands the range of viable material candidates available to tackle different loss channels in superconducting circuits [1]. Recently, we explore superconducting gap engineering in Ta-based devices as a powerful strategy for expanding the range of suitable host materials. By alloying 20 at.% hafnium (Hf) into Ta thin films, we achieve a superconducting transition temperature (Tc) of 6.09 K as observed in direct current (DC) transport measurements, reflecting an increase in the superconducting gap. Here we demonstrate an approach for controlling varying deposition conditions to control film orientation and transport properties of Ta and Ta-Hf alloy thin films. We investigate the microstructure and composition distribution of the thin films by using high-resolution scanning transmission electron microscopy (STEM) with super-X EDS system (no serious beam damage issue [6-8]). Our structural analysis using TEM diffraction and STEM verifies the BCC structure across all the films (Figure 1), and direct current (DC) transport measurements reveal a 40% enhancement in Tc relative to undoped Ta (Tc=4.3 K). We monitored oxide growth over an 18-day period following film deposition to better understand how Hf incorporation influences surface oxides. In both Ta and Hf spectra, the fraction of fully oxidized (Ta2O5 and HfO2) states gradually increased during the 18-day exposure, indicating progressive surface oxidation. To estimate the surface oxide thickness, we use cross-sectional TEM/EDS mapping (Figure 1c). The analysis reveals that the oxide thickness for the 1 ks Ta-Hf alloy film is approximately 3 nm in thickness, comparable to the 3 nm oxide observed on native Ta [2]. For the 2 ks Ta-Hf film, the oxide thickness increases slightly to about 4 nm (Figure 1). The measured surface loss tangent of the Ta-Hf alloy remains comparable to that of native Ta. This result suggests that the surface oxide of the Ta-Hf alloy, which contains a measurable fraction of HfOx, does not introduce additional dielectric loss. By engineering the alloy composition and film deposition, this study achieves both improved superconducting properties and compatibility with fabrication processes. These findings show that material doping and alloying can strategically expand the suite of viable materials for superconducting quantum devices. This approach provides a pathway for tailoring material properties to support the next generation of quantum technologies and offers broad relevance to researchers in materials science, quantum information, and device engineering [9]. STEM images on cross sections of 1 ks (a) and 2 ks (b) Ta-Hf thin films, both films were sputtered at 750 ◦C. (c) Cross-sectional EDS elemental mapping on Ta-Hf. Cross-sectional EDS mapping Ta (blue) and Hf (orange) confirmed a uniform Ta-Hf alloy with the Ta to Hf atomic ratios for the bulk to be (83% : 17%). The oxygen (red) map reveals a surface oxide layer with the estimated surface oxide thickness of around 4 nm. The 1 ks Ta-Hf film exhibits an oxide thickness of approximately 3 nm, similar to that of native Ta. The EDS resolution limit is 0.5 atomic percent.
Superconducting qubits have become one of the leading contenders in making quantum computing a reality because of their robustness and scalability [1]. Replacing the widely adopted Al and Nb, Ta has become the most promising candidate material for superconducting qubit fabrication due to its exceptionally enhanced thermal relaxation time (i.e., T1 time). This time can exceed 0.3 milliseconds which is three orders of magnitude higher than the previous methods [2]. However, during the fabrication process, exposure of tantalum to air leads to the formation of an amorphous surface oxide layer. The presence of this oxide layer can affect the superconducting properties of the tantalum film and, hence, the performance of the qubit. This native amorphous oxidized surface results in a dielectric loss through an energy reduction mechanism called a two-level system caused by structural and chemical defects [3]. Although Ta exhibits superior performance, particularly T1 time, compared to other superconducting materials, its value remains insufficient for quantum processor hardware. Therefore, understanding the structural and chemical profile of the native amorphous surface of the oxides for superconducting qubits is required to optimize their performance. In this study, we employed scanning transmission electron microscopy (STEM) with a combination of electron energy loss spectroscopy (EELS) and four-dimensional STEM (4D-STEM) to probe the electronic and crystallographic structure of the local surface areas. Furthermore, to circumvent the spectral and diffractometric profiles that overlap as a function of depth position caused by electron beam broadening, we applied Multivariate curve resolution (MCR) analysis that can separate complex mixtures into their basis components. In the subsequent experiments, we investigated the surface morphology of (110)-oriented α-Ta film grown on an A-plane sapphire substrate using scanning electron microscopy (SEM) (Figure 1a), and high-angle annular dark-field (HAADF) STEM imaging (Figure 1b and 1c). We found that the surface of the Ta film is bumpy, and made of an amorphous material with a thickness of about 3 nm. The film exhibits a columnar structure along the [001] growth direction. EELS fine structure analysis reveals that most of the amorphous regions are in the Ta2O5 phase (Figure 2a and 2b). By extracting valuable basis components of O-K fine structures, we were able to quantify the concentration of the chemical species with Å-scale at the interface using MCR analysis. Specifically, a depth dependent composition variation, especially that of oxygen concentration, was observed. We further investigated amorphous oxide films and interfaces with 4D-STEM based fluctuation electron microscopy. (Figure 2c and 2d) We obtained results that were consistent with the chemical profiles obtained from the O-K edge EELS mapping. We also revealed the crystalline ordering information of each chemical species. The detailed descriptions of the results will be presented at the conference. These STEM analysis findings were supported by first-principles calculations of oxygen concentration changes and phase formation energies. Overall, our research provides important insights into the formation and properties of the native amorphous surface oxides of a superconducting qubit tantalum film, which is critical for the development of next-generation quantum computing technologies [4]. Surface morphology of α-Ta film on A-plane sapphire. (a) Top-view SEM image. Cross-sectional HAADF STEM images at (b) low and (c) high magnification. To protect the film surface during the FIB process, the coating layer is on top of the bumpy surface of the Ta film with a thin native oxidized layer of gray contrast. Crystal orientation is indicated on the left-bottom corner in (a) and (c) for the top-view and cross-sectional view images, respectively. STEM-EELS and 4D-STEM analysis across the interfaces between the native oxidized amorphous and the crystalline Ta film. (a) HAADF STEM image of the region-of-interest, simultaneously acquired with EELS mapping. (b) Representative EELS spectra of O-K edge fine structures and (c, d) electron diffraction patterns from the native oxidized amorphous region (green) and the crystalline Ta film region (blue).
Improving qubit lifetime is essential for fault-tolerant quantum computing. It is widely acknowledged that intricate processing techniques introduce defects at the interfaces and surfaces of superconducting quantum circuits, which can create sources of decoherence. Therefore, a precise understanding of how a material's structure contributes to decoherence is critical for enhancing the performance of superconducting qubits. This talk highlights our recent advancements in understanding surface oxides in resonators and ultrathin aluminum oxide barriers in Josephson junctions (JJs) using transmission electron microscopy and spectroscopy techniques [1-4]. The Superconducting Quantum Materials & Systems Center (SQMS) demonstrated that encapsulating niobium surfaces with a ∼10nm tantalum layer results in 2-5x longer T1 than bare niobium [2]. Our collaborative investigation shows that this improvement is attributed to tantalum's less lossy surface oxide, which contains fewer sub-oxides than niobium oxide. Moreover, the amorphous Ta2O5 shows a bonding nature closer to crystalline form than amorphous Nb2O5, potentially reducing hydrogen diffusion toward the oxide/metal interface [1, 2]. Moreover, we will briefly discuss our preliminary study of the thin film structure under cryogenic conditions down to 20K, conducted using a liquid helium TEM holder in a Thermo Cs-corrected Titan. We also explored the effect of aluminum deposition rates on aluminum oxide microstructure and qubit lifetime. Although increasing the deposition rate from 0.5 Å/s to 5 Å/s significantly improved oxide layer roughness and thickness variation, the qubits’ coherence remained unchanged. This is likely due to Cooper pairs only tunneling through the thinnest parts of the barrier, making them less affected by the grain boundaries in the thin aluminum films. Additionally, we uncovered a stress-induced grain boundary sliding mechanism, which contributes to short-circuit failures in JJs [4]. Our discovery provides vital insight into oxide microstructure and superconducting qubits’ functionality [5].