Nanophotonics with single defect centres in nanodiamonds for quantum technologies

Schröder, Schell, Gadeke +3 more

Tim Schröder, Friedemann Gädeke, Moritz J. Banholzer +1 more

Single photons are fundamental elements for quantum information technologies such as quantum cryptography, quantum information storage and optical quantum computing. Colour centres in diamond have proven to be stable single-photon sources and thus essential components for reliable and integrated quantum information technology. A key requirement for such applications is a large photon flux and a high efficiency. Paying tribute to various attempts to maximize the single-photon flux, we show that collection efficiencies of photons from colour centres can be increased with a rather simple experimental setup. To do so, we spin-coated nanodiamonds containing single nitrogen-vacancy (N-V) colour centres on the flat surface of a ZrO 2 solid immersion lens. We found stable single-photon count rates of up to 853 kcts s − 1 at saturation under continuous wave excitation while having access to more than 100 defect centres with count rates from 400 to 500 kcts s − 1 . For a blinking defect centre, we found count rates up to 2.4 Mcts s − 1 for time intervals of several tens of seconds. It seems to be a general feature that very high rates are accompanied by blinking behaviour. The overall collection efficiency of our setup of up to 4.2% is the highest yet reported for N-V defect centres in diamond. Under pulsed excitation of a stable emitter of 10 MHz, 2.2% of all pulses caused a click on the detector adding to 221 kcts s − 1 thus, opening the way towards diamond-based on-demand single-photon sources for quantum applications.

Yiwen Chu, Nathalie P. de Leon, Ruffin E. Evans +9 more

Simeon Bogdanov

Jack Aspinall, Sanmi Adekanye, Imogen Brown +2 more

Colour centres in nanodiamonds provide robust sources of fluorescence and can be used as triggered sources of single photons at room temperature. However, practical devices require stability over thousands of hours of operation, and the use of strong pulsed optical excitation, placing significant burden on the robustness of the emitters that requires bespoke testing. In this work we report the response of single NV centres in nanodiamonds of 50 nm and 100 nm diameter to accelerated lifetime testing, exciting the defects close to saturation around 1013 times to simulate the minimum operational lifetime of a practical device. For nanodiamonds 50 nm in diameter, observed changes in the fluorescence intensity and lifetime suggest a progressive size reduction as a result of the pulsed laser excitation, combined with the introduction of non-radiative centres on or near the nanodiamond surface which affect the quantum efficiency of the NV centre and ultimately lead to photobleaching of the emission. We find examples of NV centres in 100 nm nanodiamonds for which triggered single photon emission remains stable for over these accelerated lifetime tests, demonstrating their suitability for use in practical devices.

Tim Schröder, Masazumi Fujiwara, Tetsuya Noda +3 more

We present a fiber-coupled diamond-based single photon system. Single nanodiamonds containing nitrogen vacancy defect centers are deposited on a tapered fiber of 273 nanometer in diameter providing a record-high number of 689,000 single photons per second from a defect center in a single-mode fiber. The system can be cooled to cryogenic temperatures and coupled evanescently to other nanophotonic structures, such as microresonators. The system is suitable for integrated quantum transmission experiments, two-photon interference, quantum-random-number generation and nano-magnetometry.