OPTICAL ABSORPTION SPECTRUM OF EXCITED Cr3+IONS IN YTTRIUM ALUMINUM GARNET
B. K. Sevast’yanov, D. T. Sviridov, V. P. Orekhova +3 more
An investigation was made of the absorption spectrum of Cr 3+ ions in the ground ( 4 A 2 ) and metastable ( 2 E) states, and of the luminescence spectrum of the same ions in Y 3 Al 5 O 12 crystals at 300 and 77°K. The effective absorption cross sections were determined for the 4 A 2 state. The luminescence deexcitation time was found to be 1.5 and 9 msec at 300 and 77°K, respectively. The absorption spectrum of the 2 E state had four wide absorption bands with maxima at 16,700, 23,300, 28,600, and 40,500 cm –1 . The theoretical energy level scheme of Cr 3+ was calculated for Dq = 1725 cm –1 , G = 640 cm –1 , C = 3200 cm –1 , v = 495 cm –1 , and v' = 259 cm –1 , making an allowance for the mixing of the Γ trig S states. The experimentally observed absorption bands were attributed to specific transitions and the theoretical and experimental intensities were compared.
Soviet Journal of Quantum Electronics•Apr 30, 1973•13 citations