Increasing the detection efficiency (DE) is a hot issue in the development of the superconducting nanowire single photon detector (SNSPD). In this work, a cavity-integrated structure coupled to the SNSPD is used to enhance the light absorption of nanowire. Ultra-thin Nb films are successfully prepared by magnetron sputtering, which are used to fabricate Nb/Al SNSPD with the curve of 100 nm and the square area of 4 × 4 μm 2 by sputtering and the lift-off method. To characterize the optical and electrical performance of the cavity-integrated SNSPD, a reliable cryogenic research system is built up based on a He 3 system. To satisfy the need of light coupling, a packaging structure with collimator is conducted. Both DE and the dark count rates increase with l b . It is also found that the DE of SNSPD with cavities can be up to 0.17% at the temperature of 0.7K under the infrared light of 1550 nm, which is obviously higher than that of the SNSPD directly fabricated upon silicon without any cavity structure.
Increasing the detection efficiency (DE) is a hot issue in the development of the superconducting nanowire single photon detector (SNSPD). In this work, a cavity-integrated structure coupled to the SNSPD is used to enhance the light absorption of nanowire. Ultra-thin Nb films are successfully prepared by magnetron sputtering, which are used to fabricate Nb/Al SNSPD with the curve of 100 nm and the square area of 4 × 4 μm 2 by sputtering and the lift-off method. To characterize the optical and electrical performance of the cavity-integrated SNSPD, a reliable cryogenic research system is built up based on a He 3 system. To satisfy the need of light coupling, a packaging structure with collimator is conducted. Both DE and the dark count rates increase with l b . It is also found that the DE of SNSPD with cavities can be up to 0.17% at the temperature of 0.7K under the infrared light of 1550 nm, which is obviously higher than that of the SNSPD directly fabricated upon silicon without any cavity structure.
We have developed a practical superconducting nanowire single photon detector (SNSPD) system with our superconducting thin films and devices fabrication, optical coupling packaging, and cryogenic technology. The SNSPD devices were fabricated from high-quality niobium nitride (NbN) ultra-thin films that were epitaxially grown on single-crystal MgO substrates, and optical cavity structure were applied for improvement of photo absorption efficiency. The SNSPD system was developed based on a compact Gifford-McMahon (GM) cryocooler, in which SNSPD can operate continuously at temperature of 2.9 K +/- 10 mK with low power consumption without any liquid cryogens. The system detection efficiencies at 1550 nm wavelength (at a 100 Hz dark count rate) were found to be 2.6% for device without optical cavity and 21% for device with optical cavity. The response speed of devices showed maximally 200 MHz with 5 × 5 mm square device, and timing jitter of 100 ps full width at a half maximum (FWHM) was observed.
Single photon detection advanced rapidly in the last decade. The superconducting nanowire single-photon detector (SNSPD) is an emerging technology, which offers low dark count rates, broadband sensitivity from visible to mid-infrared wavelengths and very high quantum efficiency. All these features are appealing for future emerging applications in remote gas sensing, quantum key distribution and quantum information processing. By enclosing the detector in an optical cavity, tuned to the operating wavelength, the total system detection of the SNSPD is improved. Based on the cavity design, the detector absorption is boosted at the desired experimental wavelength. Devices have been fabricated and tested, in this thesis, with enhanced detection efficiency at near-infrared, infrared and mid-infrared wavelengths. NbTiN detectors fabricated on Ta2O5 / SiO2 distributed Bragg reflectors (DBR) for front-side coupling exhibit a system detection efficiency of ≈ 90% at λ = 940 nm for the best device measured. SNSPDs were also fabricated in NbTiN on metallic mirrors for back-side coupling for 1550 and 2333 nm experimental wavelengths. The first design exhibited a system detection efficiency of ≈ 84.5%, at λ = 1550 nm for the best device measured. The second exhibited low system detection efficiency since the device suffered from unexpectedly high dark count rate mainly due to blackbody radiation at 2.2 K. However, it was possible to measure the timing jitter of this device at 350 mK indicating a FWHM of 84 ps. Another technique to improve the total system detection efficiency of the SNSPD, is by fabricating a hairpin-shaped nanowire atop a single mode waveguide. In this design, photons travel through the waveguide and via evanescent coupling are absorbed in the nanowire. These SNSPD devices have been designed to thread along single mode Si ridge waveguides using a hairpin-shaped nanowire structure, which offers enhanced coupling and absorption efficiency via evanescent coupling. These ultra-thin superconducting MoSi detectors are precisely patterned on top of a single mode Si waveguide (600 nm) with alignment error less than 40 nm. Low temperature electrical and nano-optical characterization was carried out using a two-stage pulse tube (PT) coldhead, using an additional 4He / 3He sorption pump, low vibration characterization of SNSPD devices at 350 mK was carried out. Characterised devices exhibit low dark count rate <5 counts per second and timing jitter of ≈ 83 ps full width half maximum (FWHM) at wavelength (λ) = 1550 nm and at critical current ≈ 30 µA.
We report on the enhancement of system detection efficiency in a superconducting nanowire single-photon detector (SNSPD) by applying the optical cavity structure. The nanowire was made using 4-nm-thick NbN thin films and covered with an SiO cavity and Au mirror designed for 1300-1600nm wavelengths. The device is mounted into fiber-coupled packages, and installed in a practical multichannel system based on GM cryocoolers. System detection efficiency depends on the absorptance of cavity structure, and reached 28% and 40% at 1550nm and 1310nm wavelengths, respectively. These values were considerably higher than an SNSPD without optical cavity.
We developed superconducting nanowire single-photon detectors with an optical cavity (OC-SNSPDs) for multichannel systems. For efficient coupling, the devices were installed in compact fiber-coupled packages after their substrate thickness was reduced from 400 to 45 microm. The measured detection efficiency (DE) measurement at different substrate thicknesses and the estimation of optical coupling efficiency indicated that approximately 98% of the input light beam could be radiated on a 15 x 15 microm2 nanowire area from behind the substrate. The DEs of a NbN OC-SNSPD system were observed to be 9.5% and 25% at 1550 nm and 1310 nm, respectively (dark-count rate: 100 c/s).
Ever since superconducting nanowire single-photon detectors (SNSPDs or SSPDs) were demonstrated, they have attracted a considerable attention due to the detectors’ promising performance that includes high detection efficiency (DE), low dark count rate (DCR), broadband sensitivity, and low timing jitter. The system detection efficiency (SDE) has been improved to be over 90% with a wavelength of 1550 nm in a fiber-coupled system by embedding the SNSPD in optical cavities. However, the implementation of optical cavity usually reduces the bandwidth of SNSPDs. As a result, there are some recent works on increasing the bandwidth of SNSPD. Furthermore, the size of the active area of meandered nanowires has to be compatible with the core size of an optical fiber such that good optical coupling can be achieved; this setup requires a long nanowire with a large kinetic inductance, thus resulting in a small counting rate and a large timing jitter, particularly for multi-mode fiber-coupled devices. Nevertheless, a particularly impressive waveguide-coupled SNSPD has been developed in recent years. By placing an SNSPD atop an optical waveguide that has been fabricated on various substrate materials, photons propagating in the waveguide have been found to be evanescently absorbed by nanowires that are only a few tens of microns long. The on-chip DE of this device has been estimated to be over 90%, thus indicating that it has both high absorptance and high intrinsic DE. If the waveguide and the nanowire are correctly dimensioned, the absorptance of this device can reach over 90% for a wavelength range of more than 700 nm. Furthermore, the length of the nanowire is shorter than that of the fiber-coupled SNSPD, thus leading to a higher count rate and lower timing jitter (~18 ps). However, unsatisfactory coupling losses between the optical fiber and the waveguide in such devices can decrease its SDE (~10%), thus limiting its applicability to quantum photonic integrated circuits (QPIC). Recently, we proposed a type of SNSPD that was coupled with microfibers (MFs), and simulations for this SNSPD indicated that its absorption would be as high as 90%. Microfibers and nanofibers, tapered adiabatically from standard fibers, with diameters close to or smaller than the wavelength of the guided light were demonstrated to have low transmittance losses by Tong et al. in 2003. MFs have been shown to have many interesting properties, such as strong evanescent fields, tight optical confinement, wideband abilities, and small masses; these properties are appealing for applications such as optical sensing and coupling. MFs also provide seamless connections with high transmittance from standard fibers; therefore, MF-coupled SNSPDs can achieve both high SDEs and wideband compatibility. We proposed and demonstrated the MF-coupled SNSPDs successfully. The simulation results indicate that with optimal device structure, the optical absorption with efficiency < 90% can be realized over a wavelength range of 350 nm to 2150 nm. The fabricated MF-coupled SNSPD, shows unparalleled broadband system detection efficiencies (SDEs) of more than 50% from 630 nm to 1500 nm. The SDEs reach 66% at 785 nm and 45% at 1550 nm. These results pave the way for ultra-broadband weak light detection with quantum-limit sensitivity.
Superconducting nanowire single photon detectors with an optical resonant cavity structure are fabricated directly on the single crystal substrate. In order to enhance the photons absorption of incident light and improve system detection efficiency (SDE) efficiently, the structure of SNSPD was designed and optimized using the finite-difference time-domain analysis for different kinds of substrates. The NbN-SNSPDs fabricated on different substrates are measured and compared. The SDE of NbN-SNSPD on MgO substrate reaches 66 % at the wavelength of 940nm at a dark count rate of 100 cps by illuminating from the back of the device through single mode optical fiber.