We have measured the characteristics of a novel SQUID magnetometer pumped at 9 GHz. The device comprises a niobium point-contact shunting a low impedance superconducting microwave transmission line which isolates the junction at high frequencies from a toroidal input transformer. The junction is matched to a 50 Ω coaxial transmission line and the SQUID is operated in a reflection mode. For low values of the weak link critical current we observe a modulation of the phase of the reflected microwave signal periodic in the applied flux. The modulation persists at high microwave power levels indicating that the junction response is maintained to at least 200 GHz. For large values of critical current, amplitude modulation is observed. We have obtained a differential sideband power of 230 pW/(\Phi_{0})^{2}which is close to the value predicted by a simple model. In flux-locked loop operation we have obtained an energy sensitivity referred to the input terminals of 7 × 10-31J/Hz, which is superior to that so far reported for any other SQUID.
We have measured the characteristics of a novel SQUID magnetometer pumped at 9 GHz. The device comprises a niobium point-contact shunting a low impedance superconducting microwave transmission line which isolates the junction at high frequencies from a toroidal input transformer. The junction is matched to a 50 Ω coaxial transmission line and the SQUID is operated in a reflection mode. For low values of the weak link critical current we observe a modulation of the phase of the reflected microwave signal periodic in the applied flux. The modulation persists at high microwave power levels indicating that the junction response is maintained to at least 200 GHz. For large values of critical current, amplitude modulation is observed. We have obtained a differential sideband power of 230 pW/(\Phi_{0})^{2}which is close to the value predicted by a simple model. In flux-locked loop operation we have obtained an energy sensitivity referred to the input terminals of 7 × 10-31J/Hz, which is superior to that so far reported for any other SQUID.
A high-sensitivity microwave SQUID (superconducting quantum interference device), suitable for RF attenuation measurements, is constructed taking advantage of the low density of states of current carriers in high-T/sub c/ materials. The dynamics, the noise properties, and the sensitivity of the microwave SQUID are theoretically analyzed. The ultimate energy resolution of the waveguide SQUID is inversely proportional to the characteristic frequency omega /sub c/=R/sub q//L of the loop. omega /sub c/ is high for YBaCuO junctions at 4.2 K because of small leakage. A flux sensitivity of 4*10/sup 4-6/ phi /sub 0// square root Hz has been achieved, which is in good agreement with the theoretical predictions.>
The operation and noise limitations of de and RF SQUID's are outlined, and recent advances in their sensitivity are discussed. A model of the dc SQUID predicts an energy noise level per hertz referred to the SQUID of approximately8 k_{B}TL/R \approx 8 k_{B}T(\piLC)^{1/2}, whereL, R,andCare the SQUID inductance and the shunt resistance and capacitance of each Josephson junction. Some examples of dc SQUID's are described to show that their performance is generally in reasonable agreement with the model. The noise energy has improved from about 2 × 10-30J. Hz-1for a device withL = 1nH and a tunnel junction area of 104µm2to about 2 × 10-33J . Hz-1for a device withL = 0.1nH and a microbridge resistance of 40 Ω. Further improvements axe expected in the near future. The model of the RF SQUID predicts a noise energy per hertz referred to the SQUID of[(\pi\alpha^{2}\phi\min{0}\max{2}/2L) + 2 \pi \alpha k_{B}T\min{a}\max{(eff)}]/\omega_{RF}, where α is the intrinsic width of the distribution of flux transitions,T\min{a}\max{(eff)}is an effective amplifier noise temperature, and ωRFis the pump frequency. With one exception, the performance of the seven types of RF SQUID listed is in reasonable agreement with the model. The noise energy ranges from about 1.5 × 10-29J . Hz-1for a 20-MHz toroidal SQUID to 3.5 × 10-31J . Hz-1for 9-GHz reentrant toroidal SQUID; a somewhat better sensitivity has been reported for a 430-MHz device, apparently in conflict with the theory. In both dc and RF SQUID's, 1/fnoise (fis frequency) is likely to extend to higher frequencies as the white-noise level is decreased.
We have designed and characterized a micro-SQUID with dispersive readout for use in low temperature scanning probe microscopy systems. The design features a capacitively shunted RF SQUID with a tunable resonance frequency from 5 to 12 GHz, micrometer spatial resolution, and integrated superconducting coils for local application of magnetic fields. The SQUID is operated as a nonlinear oscillator with a flux- and power-dependent resonance frequency. Measurements for device characterization and noise benchmarking were carried out at 4 K. The measured flux noise above 10 kHz at 4 K is 80 nΦ0 Hz−1∕2 at a bandwidth of 200 MHz. Estimations suggest that one can benefit from parametric gain based on inherent nonlinearity of the Josephson junction and reduce the flux noise to 30 nΦ0Hz–1∕2 at 100 mK, which corresponds to 10.6 μBHz–1∕2 for a magnetic moment located at the center of the pickup loop.Measuring the magnetic response of mesoscopic samples or mapping it vs. position for extended systems is effective methods for revealing the fundamental quantum properties of condensed matter systems. Over the past few decades, many advanced magnetic imaging schemes have been developed, including magnetic force microscopy,1 scanning Hall probe microscopy,2 superconducting interference devices (SQUIDs),3,4 and NV center based magnetometry.5 The high sensitivity, low back action, and low power dissipation of SQUIDs make them attractive for many types of low temperature experiments. One classic example is the central role of scanning SQUID microscopy in tests of pairing symmetry of high-Tc cuprate superconductors.6 Other prominent applications are the thermodynamic characteristics of persistent currents in normal metal rings7 and proof of edge states in topological insulators in the quantum spin Hall regime.8A key performance for a SQUID is its flux sensitivity. Parametric amplification has been harnessed in nano-SQUIDs based on aluminum junctions9,10 in order to reduce the flux noise down to 30 nΦ0Hz–1∕2 with a bandwidth exceeding 60 MHz.10 Recent studies on parametric amplifiers and dispersive readout of superconducting qubits also harness the nonlinearity of the Josephson junction to boost sensitivity.11–13In scanning SQUID microscopy, signal sources often behave dipole-like, such as superconducting vortices in mesoscopic dots or currents in mesoscopic rings. Smaller SQUIDs provide better coupling to smaller samples which leads to higher spin sensitivity3,14 as the magnetic field of a dipole decreases with 1/r3. Various approaches have been pursued to reduce the size. The smallest nano-SQUID to date has been fabricated by evaporating Nb or Pb15 onto the apex of a sharp quartz tip reaching a loop diameter of below nm and a spin sensitivity of 0.38 μBHz−1/2 at tens of kHz bandwidth. Compared to such size-optimized devices, micro-SQUIDs fabricated using a standard Nb technique have the advantage of on-chip field coils and modulation coils,14 and can be operated at 4 K allowing for a wide range of applications. However, these come at the cost of larger pick-up loops of a few microns and a resulting poorer spin sensitivity of 200 μBHz−1/2 for a magnetic moment located at the center of the pickup loop.The limitation of large pickup loops was previously only overcome by devices with pickup loops defined by the focused-ion-beam,16 but has recently also been achieved by improvements in lithography and shown to offer better spatial resolution as well.17 Here, we present a scanning micro-SQUID which is based on the same fabrication technology incorporating another major advancement. Our design exploits the parametric amplification based on nonlinearities of the SQUID to boost sensitivity. The combination of a smaller pickup loop and parametric amplification of the signal leads to better spin sensitivity (10.6 μBHz−1/2) and higher bandwidth (200 MHz) compared to traditional DC micro-SQUIDs in which the flux sensitivity is mainly limited by internal dissipation.Our devices were fabricated at Hypres Inc. using planarized Nb/AlOx/Nb trilayer Josephson junction technology, including two planarized Nb layers with approximately 0.8 μm minimum feature size. The SQUID consists of a superconducting ring shunted by one Josephson junction with a designed critical current of 20 μA [Fig. 1(a)]. With this geometry, the SQUID is gradiometric, i.e., the effect of any homogeneous background magnetic field approximately cancels out. The smallest pickup loops implemented have an inner (outer) diameter of 1 μm (2 μm). The superconducting loop is shunted by an on-chip parallel-plate capacitor with amorphous silicon dioxide as dielectric which was designed to have a capacitance of 80 pF. The superconducting loop and the capacitor form a resonator with a flux dependent resonance frequency from 5 to 12 GHz. The pickup loops are placed on opposite corners of the parallel-plate capacitor at a distance of about 450 μm so that one loop can be located in close proximity to the sample while the other is kept far away from it. External fields can be applied to the sample by local single-turn field coils situated around each pickup loop. The field coils are fully integrated into the chip layout and can also be used to bias the SQUID at its most sensitive point. Compared to using additional modulation coils,14 this approach has the advantage of reducing the total device inductance, which leads to a higher sensitivity.18 In a scanning microscope, the field coil at the rear end (away from the sample) can be used to bias the SQUID or operate it in flux feedback such that resulting stray fields will not act on the sample, apart from a weak screening current through the pickup loop. The effective diameter of each coil is 7.5 μm, resulting in a mutual inductance of about 0.34 Φ0/mA (for the smallest pickup loop). The SQUID resonator is connected by an on-chip Z0 = 50 Ω coplanar waveguide (CPW) transmission line to the bonding pads. The two field coils are connected by two smaller CPWs to the bottom edge bonding pads [Fig. 1(c)], ending in two parallel-stripline waveguides running alongside the edges of the capacitor towards the respective field coils. Based on estimations, it should thus be possible to apply high frequency signals of at least several GHz to SQUID and sample.
A superconducting quantum interferometer device (SQUID) electronics with tank frequencies near 150 MHz was constructed to enhance the rf SQUID sensitivity. By these means we characterized our YBa2Cu3O7 thin-film rf SQUIDs with step-edge junctions immersed in liquid N2. We obtained transfer function values of over 40 μV/Φ0, at a 50 Ω input impedance, for both hysteretic and dispersive mode of rf SQUID operation. The rms white and 1/f flux noise levels were significantly lower than at the tank frequency of 20 MHz. The best magnetic field sensitivity at 77 K was 0.9 pT/Hz1/2, and the energy resolution 1.4×10−28 J/Hz, down to 0.3 Hz.
The dynamics and noise of a dc SQUID (the Superconducting Quantum Interference Device), with the McCumber parameter /spl beta//sub c/=2/spl pi/R/sup 2/l/sub c/C//spl Phi//sub 0/ close to the unity (where I/sub c/, R, C is the critical current, the shunt resistance and the capacitance of the Josephson junctions comprising the SQUID, respectively, /spl Phi//sub 0/=2.07 10/sup -15/ Wb is the magnetic flux quantum) integrated with a planar spiral input coil, have been experimentally studied. The length of the spiral input coil was chosen so as to match its /spl lambda//4 microwave resonance frequency to the plasma resonance frequency of the SQUID. The input coil resonance is found to enhance the overall quality factor Q of the Josephson oscillations in the SQUID and, as a result, to increase the dynamic resistance R/sub d/ and the gradient of the flux-to-voltage characteristics, /spl delta/V//spl delta//spl Phi/, without hysteresis. A dc SQUID with a loop inductance L=30.5 pH, /spl beta//sub c/=0.72, and a 6 turn input coil demonstrated a non-distorted quasi-sinusoidal flux-to-voltage transfer function with an exceptionally large modulation depth of 140 /spl mu/V peak-to-peak. The spectral density of the magnetic flux noise was as low as 3.5/spl times/10/sup -7/ /spl Phi//sub 0//Hz/sup 1/2/ in the double stage configuration, measured at a temperature 4.2 K using direct read out electronics. In combination with an intermediary transformer, the current resolution of the SQUID is as low as 1.25 pA/Hz/sup 1/2/ with an input coil inductance of 100 nH.
There is currently fundamental and technological interest in measuring and manipulating nanoscale magnets, particularly in the quantum coherent regime. To observe the dynamics of such systems one requires a magnetometer with not only exceptional sensitivity but also high gain, wide bandwidth, and low backaction. We demonstrate a dispersive magnetometer consisting of a two-junction superconducting quantum interference device (SQUID) in parallel with an integrated, lumped-element capacitor. Input flux signals are encoded as a phase modulation of the microwave drive tone applied to the magnetometer, resulting in a single quadrature voltage signal. For strong drive power, the nonlinearity of the resonator results in quantum limited, phase sensitive parametric amplification of this signal, which improves flux sensitivity at the expense of bandwidth. Depending on the drive parameters, the device performance ranges from an effective flux noise of 0.29 $\ensuremath{\mu}{\ensuremath{\Phi}}_{0}$Hz${}^{\ensuremath{-}1/2}$ and 20 MHz of signal bandwidth to a noise of 0.14 $\ensuremath{\mu}{\ensuremath{\Phi}}_{0}$Hz${}^{\ensuremath{-}1/2}$ and a bandwidth of 0.6 MHz. These results are in excellent agreement with our theoretical model.