We report the fabrication and electrical characteristics of self-shunted Josephson junctions consisting of NbN electrodes, an AlN barrier, and an NbNx normal layer for an SFQ circuit application. To fabricate such junctions with a high characteristic voltage V c, we have studied their preparation conditions including the surface treatments of MgO substrates. Junction characteristics at 4 K were dependent on the electrical properties and film thickness of the NbNx layer; the underdamped junctions changed into overdamped ones with an increase in the film thickness. The overdamped junctions showed a characteristic voltage Vc of 0.8 mV and a critical current density Jc of 22 A/cm2 at 4.2 K.
Self-Shunted NbN Junctions With NbNx/AlN Bilayered Barriers for 4 K Operation
We report the fabrication and electrical characteristics of self-shunted Josephson junctions consisting of NbN electrodes, an AlN barrier, and an NbNx normal layer for an SFQ circuit application. To fabricate such junctions with a high characteristic voltage V c, we have studied their preparation conditions including the surface treatments of MgO substrates. Junction characteristics at 4 K were dependent on the electrical properties and film thickness of the NbNx layer; the underdamped junctions changed into overdamped ones with an increase in the film thickness. The overdamped junctions showed a characteristic voltage Vc of 0.8 mV and a critical current density Jc of 22 A/cm2 at 4.2 K.
We describe the fabrication processes and electrical characteristics of two types of NbN junctions. One is a self-shunted NbN/NbNx/AlN/NbN Josephson junction, which is expected to improve the density of integrated circuits; the other is an underdamped NbN/AlNx/NbN tunnel junction with radical-nitride AlNx barriers, which has highly controllable junction characteristics. In the former, the junction characteristics were changed from underdamped to overdamped by varying the thickness of the NbNx layer. Overdamped junctions with a 6-nm-thick NbNx film exhibited a characteristic voltage of Vc =0.8mV and a critical current density of Jc =22A/cm2 at 4.2K. In the junctions with radical-nitride AlNx barriers, Jc could be controlled in the range 0.01-3kA/cm2 by varying the process conditions, and good uniformity of the junction characteristics was obtained.
To increase the integration scale of superconductor electronics, we are developing a new node, titled SFQ7ee, of the fabrication process at MIT Lincoln Laboratory. In comparison to the existing SFQ5ee node, we increased the number of fully planarized superconducting layers to ten and utilized NbN and NbN/Nb kinetic inductors to increase the possible inductor number density above a hundred million inductors per cm2. Increasing the Josephson junction number density to the same level requires implementing self-shunted high-JcJosephson junctions. We investigated the properties of Nb/NbNx/Nb trilayer junctions as a potential replacement of high-JcNb/Al-AlOx/Nb junctions, where NbNxis a disordered, overstoichiometric, nonsuperconducting nitride deposited by reactive sputtering. Dependences of theIcRnproduct and Josephson critical current density, Jc on the NbNx barrier thickness and temperature were studied in the thickness range from 5 nm to 20 nm. The fabricated junctions can be well described by the microscopic theory of SNS junctions, assuming no suppression of the energy gap in Nb electrodes near the NbNxinterfaces and a Cooper pair decay length in the NbNx barrier, ξnTcof about 2.3 nm. Current-voltage characteristics of the junctions are well described by the resistively and capacitively shunted junction (RCSJ) model without excess current. In the studied rangeJc2, the Nb/NbNx/Nb junctions have lower values of the specific resistanceRnA, lower IcRn products, and a stronger dependence of theIcRnon temperature than the self-shunted or critically damped externally shunted Nb/Al-AlOx/Nb junctions with the same critical current density; A is the junction area,Icthe junction critical current, and Rnthe effective shunting resistance.
Abstract In this work, we report the electrical properties of NbN internally shunted Josephson junctions with NbN x barriers. Cross-sectional scanning transmission electron microscopy analysis shows that all layers have the same cubic structure; NbN/NbN x /NbN trilayers were epitaxially grown on MgO substrates. The resistivity of the NbN x films could be varied in the range of 1–104 mΩ cm by controlling both the N2 partial pressure and the deposition time during reactive sputtering. The temperature dependence of the critical current density (J c) and characteristic voltage (I c R n) of the junctions with different barrier resistivities were measured for various barrier thicknesses. For the 10 nm-thick NbN x layer with resistivities of 73.44, 385.72, and 711 mΩ cm, the coherence length of the barrier was determined to be 5.55 ± 0.07, 4.88 ± 0.06, and 1.40 ± 0.13 nm, respectively, corresponding to carrier diffusion rates of 2.741 ± 0.004, 1.211 ± 0.002, and 0.008 ± 0.001 cm2 s−1, respectively. Thus, the reduction in barrier resistivity leads to a larger coherence length and a faster diffusion rate, which will further increase the J c and I c R n of the junction. By adjusting the barrier resistivity and thickness, the J c of the junction can be easily tuned over more than four orders of magnitude, and an I c R n value of 0.97 ± 0.07 mV was obtained at 10 K. The results indicate that the all-NbN self-shunt junction is a promising candidate in high-speed and high-temperature applications.
We have developed resistively shunted NbN junctions to realize superconducting single flux quantum circuits operating at 10 K and/or high speed. The junctions consist of epitaxial NbN/AlN/NbN tunnel junctions and molybdenum (Mo) resistors fabricated on single-crystal MgO substrates. The junction qualities are systematically investigated in a wide range of critical current density (Jc). The gap voltage and the ratio of Rsg/RN were about 5.6 mV and 11 for the junctions with the Jc of 10 kA/cm2, respectively. The overdamped Josephson junctions with parallel Mo resistors having a nominal sheet resistance showed non-hysteretic current-voltage characteristics for the junctions with Jc of 10 kA/cm2.
We have fabricated overdamped NbN Josephson junctions based on Nb/AlO x /Nb trilayer technology. The junctions have the structure of NbN/Nb/AlO x /Nb/NbN, where Nb/AlO x /Nb acts as a junction barrier. The overdamped junctions showed a critical current density J c and characteristic voltage as high as 0.44 kA/cm2 and 160 µV at 10 K, respectively. The junction characteristics at 4.2 K were investigated from the viewpoint of their dependence on the film thickness of the Nb layers. The junction uniformity was also evaluated. The standard deviation, 1-σ, was 2.1% for a series of 64 5×5 µm2 junctions at 4.2 K.
Abstract We report on the electrical properties of NbN/TaN/NbN Josephson junctions grown on thermally oxidized silicon substrates, along with the design and fabrication of superconducting single-flux-quantum (SFQ) circuits based on these NbN superconductor/normal metal/superconductor (SNS) junctions. The critical current density ( J c ) of the junctions was found to be relatively sensitive to the barrier thickness, decreasing from 108.0 ± 8.1 kA cm −2 for a 15 nm barrier to 12.8 ± 1.9 kA cm −2 for a 30 nm barrier. For a J c of approximately 24.5 ± 2.1 kA cm −2 and a barrier thickness of 25 nm, the NbN SNS junctions are self-shunted and exhibit nonhysteretic current–voltage ( I – V ) characteristics. Especially for junctions with diameter ( φ ) ranging from 0.8 to 1.6 μ m, their critical current ( I c ) falls within the range of 110–450 μ A, making them suitable for SFQ circuits. By considering the impact of excess current and incorporating it as an additional term in the conventional resistively and capacitively shunted junction model, the I – V curves of NbN SNS junctions can be precisely described, successfully minimizing the deviation between simulations and test results. The DC-SFQ and SFQ-DC interface circuits can both operate normally, and the bias margins of cell circuits such as Josephson transmission line, confluence buffer, D flip-flop, and splitter are greater than 40%. Compared to Nb superconductor/insulator/superconductor junctions, their self-shunting characteristics and relatively thick 25 nm barriers can also enhance the integration of circuits and increase the yield to complex circuits.