Nickel related optical centres in diamond created by ion implantation
Julius O. Orwa, Igor Aharonovich, Fedor Jelezko, Gopalakrishnan Balasubramanian, P. Balog, Matthew Markham, Daniel J. Twitchen, Andrew D. Greentree, Steven Prawer
Ni-related optical centres in diamond are promising as alternatives to the nitrogen vacancy (NV) centre for quantum applications and biomarking. In order to achieve the reliability and reproducibility required, a method for producing the Ni-related centres in a controllable manner needs to be established. In this study, we have attempted this control by implanting high purity CVD diamond samples with Ni and N followed by thermal annealing. Samples implanted with Ni show a new Ni-related PL peak centered at 711 nm and a well known doublet at 883/885 nm along with weak NV luminescence. The optical properties of the two Ni-related defects are investigated. In particular, an excited state lifetime of the 883/885 nm peak is measured to be 11.6 ns.
Ni-related optical centres in diamond are promising as alternatives to the nitrogen vacancy (NV) centre for quantum applications and biomarking. In order to achieve the reliability and reproducibility required, a method for producing the Ni-related centres in a controllable manner needs to be established. In this study, we have attempted this control by implanting high purity CVD diamond samples with Ni and N followed by thermal annealing. Samples implanted with Ni show a new Ni-related PL peak centered at 711 nm and a well known doublet at 883/885 nm along with weak NV luminescence. The optical properties of the two Ni-related defects are investigated. In particular, an excited state lifetime of the 883/885 nm peak is measured to be 11.6 ns.
The negatively-charged nitrogen-vacancy (NV) center is the most studied optical center in diamond and is very important for applications in quantum information science. Many proposals for integrating NV centers in quantum and sensing applications rely on their tailored fabrication in ultra pure host material. In this study, we use ion implantation to controllably introduce nitrogen into high purity, low nitrogen chemical vapor deposition diamond samples. The properties of the resulting NV centers are studied as a function of implantation temperature, annealing temperature, and implantation fluence. We compare the implanted NV centers with native NV centers present deep in the bulk of the as-grown samples. The results for implanted NV centers are promising but indicate, at this stage, that the deep native NV centers possess overall superior optical properties. In particular, the implanted NV centers obtained after annealing at 2000 °C under a stabilizing pressure of 8 GPa showed an ensemble linewidth of 0.17 nm compared to 0.61 nm after annealing at 1000 °C. Over the same temperature range, the ensemble NV−/NV0 ratio increased by a factor of ∼5, although this was accompanied by an overall decrease in the NV count.
Individual color centers in diamond are promising for near-term quantum technologies including quantum key distribution and metrology. Here we show fabrication of an as-yet uncharacterized nickel-related complex in diamond which has photophysical properties surpassing the two main-stay centers for single-photon applications, namely, the nitrogen-vacancy and the nickel-nitrogen complex (NE8) center. This center was fabricated using focused ion-beam implantation of nickel into isolated chemical vapor-deposited diamond crystals. A possible correlation of the center to a Ni/Si complex is substantiated by a coimplantation of Ni and Si into a pure bulk diamond. Room-temperature photoluminescence studies reveal a narrow emission in the near infrared region centered at 768 nm with a lifetime as short as 2 ns.
Abstract We present a high throughput and systematic method for the screening of colour centres in diamond with the aim of searching for and reproducibly creating new optical centres down to the single defect level, potentially of interest for a wide range of diamond-based quantum applications. The screening method presented here should, moreover, help to identify some already indexed defects among hundreds in diamond (Zaitsev 2001 Optical Properties of Diamond (Berlin: Springer)) but also some promising defects of a still unknown nature, such as the recently discovered ST1 centre (Lee et al 2013 Nat. Nanotechnol . 8 487; John et al 2017 New J. Phys . 19 053008). We use ion implantation in a systematic manner to implant several chemical elements. Ion implantation has the advantage of addressing single atoms inside the bulk with defined depth and high lateral resolution, but the disadvantage of producing intrinsic defects. The implanted samples are annealed in vacuum at different temperatures (between 600 °C and 1600 °C with 200 °C steps) and fully characterised at each step in order to follow the evolution of the defects: formation, dissociation, diffusion, re-formation and charge state, at the ensemble level and, if possible, at the single centre level. We review the unavoidable ion implantation defects (such as the GR1 and 3H centres), discuss ion channeling and thermal annealing and estimate the diffusion of the vacancies, nitrogen and hydrogen. We use different characterisation methods best suited for our study (from widefield fluorescence down to sub-diffraction optical imaging of single centres) and discuss reproducibility issues due to diamond and defect inhomogeneities. Nitrogen is also implanted for reference, taking advantage of the considerable knowledge on NV centres as a versatile sensor in order to retrieve or deduce the conditions and local environment in which the different implanted chemical elements are embedded. We show here the preliminary promising results of a long-term study and focus on the elements O, Mg, Ca, F and P from which fluorescent centres were found.
Abstract The negatively charged nitrogen-vacancy centre (so-called NV-centre) in diamond is one of the most promising systems for applications in quantum technologies because of the possibility to optically manipulate and read out the spin state of this defect, even at room temperature. Nevertheless, obtaining high NV densities (>500 ppb) close to the surface (5–20 nm) while maintaining good spin properties remain challenging. In this work we rely on a versatile ion implantation system allowing both implanting nitrogen using N 2 + and creating vacancies with He + ion bombardment at variable energies and fluence to create shallow NV ensembles. By optimizing the ion irradiation conditions as well as the surface preparation prior to treatment we successfully increase the amount of created colour centres while demonstrating narrow magnetic resonance linewidths.
A huge variety of optical colour centres can be found in diamond, emitting in its whole wide transparency range. Although several of these centres have been demonstrated as single-photon emitters, none of them meets all of the requirements of an ideal single-photon source. In this view, we discuss the properties of prominent optical centres, such as the nitrogen vacancy, the silicon vacancy or the so-called NE8 centre, as well as recently found centres ascribed to defects containing Ni, Si, Cr and Xe. Besides suitable intrinsic properties, it is necessary for practical applications that optical centres can be created artificially on demand. Of all known methods, only ion implantation allows for the most controlled creation of such defect centres. In this paper, we discuss how nanoscalability, that is, the nanometre placement and the deterministic creation of optical centres, can, could or cannot be achieved by the available ion implantation techniques. A fine analysis of individual optical centres is now possible, thanks to the recently developed subdiffraction optical microscopy methods.
The fabrication of luminescent defects in single-crystal diamond upon Sn implantation and annealing is reported. The relevant spectral features of the optical centers (emission peaks at 593.5, 620.3, 630.7, and 646.7 nm) are attributed to Sn-related defects through the correlation of their photoluminescence (PL) intensity with the implantation fluence. Single Sn-related defects were identified and characterized through the acquisition of their second-order autocorrelation emission functions, by means of Hanbury-Brown and Twiss interferometry. The investigation of their single-photon emission regime as a function of excitation laser power revealed that Sn-related defects are based on three-level systems with a 6 ns radiative decay lifetime. In a fraction of the studied centers, the observation of a blinking PL emission is indicative of the existence of a dark state. Furthermore, absorption dependence on the polarization of the excitation radiation with ∼45% contrast was measured. This work shed light on the existence of a new optical center associated with a group-IV impurity in diamond, with similar photophysical properties to the already well-known Si–V and Ge–V emitters, thus, providing results of interest from both the fundamental and applicative points of view.