A method for engineering thin (<100 nm) layers of homoepitaxial diamond containing high quality, spectrally stable, isolated nitrogen-vacancy (NV) centres is reported. The photoluminescence excitation linewidth of the engineered NVs are as low as 140 MHz, at temperatures below 12 K, while the spin properties are at a level suitable for quantum memory and spin register applications. This methodology of NV fabrication is an important step toward scalable and practical diamond based photonic devices suitable for quantum information processing.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.
The electronic spin associated with the nitrogen vacancy (NV) color center in diamond is an excellent candidate for a solid-state qubit functioning as a quantum register or sensor. However, the lack of thin film technologies for crystalline diamond with low impurity levels hampers the development of photonic interfaces to such diamond-based qubits. We present a method for manufacturing slabs of diamond of 200 nm thickness and several microns in extent from high-purity single crystal chemical vapor deposition diamond. We measure spin coherence times approaching 100 μ s and observe increased photoluminescence collection from shallow implant NV centers in these slabs. We anticipate these slabs to be appealing as quantum memory nodes in hybrid diamond nanophotonic systems.
We investigate native nitrogen vacancy (NV) and silicon vacancy (SiV) color centers in a commercially available, heteroepitaxial, wafer-sized, mm thick, single-crystal diamond. We observe single, native NV centers with a density of roughly 1 NV per μm3 and moderate coherence time (T2 = 5 μs) embedded in an ensemble of SiV centers. Using low temperature luminescence of SiV centers as a probe, we prove the high crystalline quality of the diamond especially close to the growth surface, consistent with a reduced dislocation density. Using ion implantation and plasma etching, we verify the possibility to fabricate nanostructures with shallow color centers rendering our material promising for fabrication of nanoscale sensing devices. As this diamond is available in wafer-sizes up to 100 mm, it offers the opportunity to up-scale diamond-based device fabrication.
We investigate native nitrogen (NV) and silicon vacancy (SiV) color centers in commercially available, heteroepitaxial, wafer-sized, mm thick, single-crystal diamond. We observe single, native NV centers with a density of roughly 1 NV per
μm3 and moderate coherence time (
T2=5μs) embedded in an ensemble of SiV centers. Low-temperature spectroscopy of the SiV zero phonon line fine structure witnesses high crystalline quality of the diamond especially close to the growth surface, consistent with a reduced dislocation density. Using ion implantation and plasma etching, we verify the possibility to fabricate nanostructures with shallow color centers rendering our diamond material promising for fabrication of nanoscale sensing devices. As this diamond is available in wafer-sizes up to
100mm it offers the opportunity to up-scale diamond-based device fabrication.
Abstract Diamond hosts a wide variety of colour centres that have demonstrated outstanding optical and spin properties. Among them, the nitrogen-vacancy (NV) centre is by far the most investigated owing to its superior characteristics, which promise the development of highly sophisticated quantum devices, in particular for sensing applications. Nevertheless, harnessing the potential of these centres mainly relies on the availability of high quality and purity diamond single crystals that need to be specially designed and engineered for this purpose. Plasma assisted chemical vapour deposition (CVD) has become a key enabling technology in this field of research. Nitrogen can indeed be directly doped in situ into a high crystalline quality diamond matrix in a controlled way, allowing the production of single isolated centres or ensembles that can potentially be integrated into a device. In this paper we will provide an overview of the requirements for synthesizing ‘quantum-grade’ diamond films using CVD. These include the reduction of impurities and surrounding spins that limit coherence times, the control of NV density in a wide range of concentrations as well as their spatial localization within the diamond. Enhancing the charge state and preferential orientation of the colour centres is also discussed. These improvements in material fabrication have contributed to positioning diamond as one of the most promising solid-state quantum systems and the first industrial applications in sensing are just starting to emerge.