Anomalous zero‐phonon line broadening of the (NV)– center in diamond

H. Nishikori, Y. Mita, Yosio Nisida, Musashi Okada, Takayoshi Nakashima

Published Mar 1, 2007• 3 citations

Publisher

Abstract

Abstract Absorption measurements were carried out on the (NV)– centers in diamond at low temperature after laser illumination. It was observed that the width of the zero‐phonon line becomes persistently more than two times larger. This characteristic phenomenon was studied in detail about excitation photon energy, illumination time, sample temperature and recovery nature. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)

DOI: 10.1002/pssc.200673724

Related papers

Low‐temperature excitons produced by two‐photon excitation in high‐purity diamond crystals

N. Naka, T. Kitamura, Junko Omachi +1 more

Abstract We have observed edge emission due to free excitons and electron–hole droplets in diamond by two‐photon excitation using subpicosecond laser pulses at 257 nm. We find that excitonic temperatures under two‐photon excitation are much lower than the case of one‐photon excitation. A minimum excitonic temperature of 3.4 K is extracted by spectral analysis. In order to understand the difference of the excitonic temperatures under two‐photon and one‐photon excitations, we discuss a heating mechanism which depends on the density distribution of the electron–hole pairs in the crystal along the laser beam. (© 2008 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)

physica status solidi (b)Oct 20, 200823 citations

Persistent hole burning of the nitrogen vacancy center and the 2.16 eV center of chemical-vapor deposited diamond

Yoshihiro Yokota, Jing Sheng, Toshimichi Ito +4 more

The persistent spectral hole burning effect has been observed for the nitrogen vacancy (NV) center and the 2.16 eV center in chemical-vapor deposited (CVD) diamond. This sideband is the first observation of spectral hole burning in CVD diamond. Holes are burned in the inhomogeneously broadened zero-phonon lines of both the centers by dye lasers. The holes were observed by photoluminescence excitation spectroscopy, with monitoring of the phonon-sideband emission, at temperatures up to 130 K for the NV center and up to 100 K for the 2.16 eV center.

Applied Physics LettersNov 2, 19929 citations

Strain broadening of the 1042-nm zero phonon line of the NV− center in diamond: A promising spectroscopic tool for defect tomography

Timur Biktagirov, Alexander N. Smirnov, Валерий Александрович Давыдов +4 more

The negatively charged nitrogen-vacancy $({\mathrm{NV}}^{\ensuremath{-}})$ center in diamond is a promising candidate for many quantum applications. Here, we examine the splitting and broadening of the center's infrared (IR) zero-phonon line (ZPL). We develop a model for these effects that accounts for the strain induced by photodependent microscopic distributions of defects. We apply this model to interpret observed variations of the IR ZPL shape with temperature and photoexcitation conditions. We identify an anomalous temperature-dependent broadening mechanism and that defects other than the substitutional nitrogen center significantly contribute to strain broadening. The former conclusion suggests the presence of a strong Jahn-Teller effect in the center's singlet levels and the latter indicates that major sources of broadening are yet to be identified. These conclusions have important implications for the understanding of the center and the engineering of diamond quantum devices. Finally, we propose that, once the major sources of broadening are identified, the IR ZPL has the potential to be a sensitive spectroscopic tool for probing microscopic strain fields and performing defect tomography.

arXiv:1701.05631Physical review. B./Physical review. BAug 18, 201716 citations

NV−–N+ pair centre in 1b diamond

Neil B. Manson, Morgan P. Hedges, M. S. J. Barson +5 more

With the creation of nitrogen (NV) in 1b diamond it is common to find that the absorption and emission is predominantly of negatively charged NV centres. This occurs because electrons tunnel from the substitutional nitrogen atoms to NV to form NV − –N + pairs. There can be a small percentage of neutral charge NV 0 centres and a linear increase of this percentage can be obtained with optical intensity. Subsequent to excitation it is found that the line width of the NV − zero-phonon has been altered. The alteration arises from a change of the distribution of N + ions and a modification of the average electric field at the NV − sites. The consequence is a change to the Stark shifts and splittings giving the change of the zero-phonon line (ZPL) width. Exciting the NV − centres enhances the density of close N + ions and there is a broadening of the ZPL. Alternatively exciting and ionizing N 0 in the lattice results in more distant distribution of N + ions and a narrowing of the ZPL. The competition between NV − and N 0 excitation results in a significant dependence on excitation wavelength and there is also a dependence on the concentration of the NV − and N 0 in the samples. The present investigation involves extensive use of low temperature optical spectroscopy to monitor changes to the absorption and emission spectra particularly the widths of the ZPL. The studies lead to a good understanding of the properties of the NV − –N + pairs in diamond. There is a critical dependence on pair separation. When the NV − –N + pair separation is large the properties are as for single sites and a high degree of optically induced spin polarization is attainable. When the separation decreases the emission is reduced, the lifetime shortened and the spin polarization downgraded. With separations of <12 A 0 there is even no emission. The deterioration occurs as a consequence of electron tunneling in the excited state from NV – to N + and an optical cycle that involves NV 0 . The number of pairs with the smaller separations and poorer properties will increase with the number of nitrogen impurities and it follows that the degree of spin polarization that can be achieved for an ensemble of NV − in 1b diamond will be determined and limited by the concentration of single substitutional nitrogen. The information will be invaluable for obtaining optimal conditions when ensembles of NV − are required. As well as extensive measurements of the NV − optical ZPL observations of Stark effects associated with the infrared line at 1042 nm and the optically detected magnetic resonance at 2.87 GHz are also reported.

arXiv:1807.08889New Journal of PhysicsOct 30, 2018129 citations

NV--NV+ pair centre in 1b diamond

Neil B Manson, Morgan P. Hedges, M. S. J. Barson +5 more

With the creation of nitrogen (NV) in 1b diamond it is common to find that the absorption and emission is predominantly of negatively charged NV centres. This occurs because electrons tunnel from the substitutional nitrogen atoms to NV to form NV−–N+ pairs. There can be a small percentage of neutral charge NV0 centres and a linear increase of this percentage can be obtained with optical intensity. Subsequent to excitation it is found that the line width of the NV− zero-phonon has been altered. The alteration arises from a change of the distribution of N+ ions and a modification of the average electric field at the NV− sites. The consequence is a change to the Stark shifts and splittings giving the change of the zero-phonon line (ZPL) width. Exciting the NV− centres enhances the density of close N+ ions and there is a broadening of the ZPL. Alternatively exciting and ionizing N0 in the lattice results in more distant distribution of N+ ions and a narrowing of the ZPL. The competition between NV− and N0 excitation results in a significant dependence on excitation wavelength and there is also a dependence on the concentration of the NV− and N0 in the samples. The present investigation involves extensive use of low temperature optical spectroscopy to monitor changes to the absorption and emission spectra particularly the widths of the ZPL. The studies lead to a good understanding of the properties of the NV−–N+ pairs in diamond. There is a critical dependence on pair separation. When the NV−–N+ pair separation is large the properties are as for single sites and a high degree of optically induced spin polarization is attainable. When the separation decreases the emission is reduced, the lifetime shortened and the spin polarization downgraded. With separations of <12 A0 there is even no emission. The deterioration occurs as a consequence of electron tunneling in the excited state from NV– to N+ and an optical cycle that involves NV0. The number of pairs with the smaller separations and poorer properties will increase with the number of nitrogen impurities and it follows that the degree of spin polarization that can be achieved for an ensemble of NV− in 1b diamond will be determined and limited by the concentration of single substitutional nitrogen. The information will be invaluable for obtaining optimal conditions when ensembles of NV− are required. As well as extensive measurements of the NV− optical ZPL observations of Stark effects associated with the infrared line at 1042 nm and the optically detected magnetic resonance at 2.87 GHz are also reported.

Nov 1, 20180 citations

Luminescence quenching and zero-phonon line broadening associated with defect interactions in diamond

G. Davies, M. D. Crossfield

The H3 zero-phonon line in diamond is generally broader when measured in absorption than in emission. It is shown that a nonradiative energy transfer from the H3 centres to nitrogen impurity accounts qualitatively for this behaviour.

Journal of Physics C Solid State PhysicsMar 14, 197316 citations

With the creation of nitrogen (NV) in 1b diamond it is common to find that the absorption and emission is predominantly of negatively charged NV centres. This occurs because electrons tunnel from the substitutional nitrogen atoms to NV to form NV−–N+ pairs. There can be a small percentage of neutral charge NV0 centres and a linear increase of this percentage can be obtained with optical intensity. Subsequent to excitation it is found that the line width of the NV− zero-phonon has been altered. The alteration arises from a change of the distribution of N+ ions and a modification of the average electric field at the NV− sites. The consequence is a change to the Stark shifts and splittings giving the change of the zero-phonon line (ZPL) width. Exciting the NV− centres enhances the density of close N+ ions and there is a broadening of the ZPL. Alternatively exciting and ionizing N0 in the lattice results in more distant distribution of N+ ions and a narrowing of the ZPL. The competition between NV− and N0 excitation results in a significant dependence on excitation wavelength and there is also a dependence on the concentration of the NV− and N0 in the samples. The present investigation involves extensive use of low temperature optical spectroscopy to monitor changes to the absorption and emission spectra particularly the widths of the ZPL. The studies lead to a good understanding of the properties of the NV−–N+ pairs in diamond. There is a critical dependence on pair separation. When the NV−–N+ pair separation is large the properties are as for single sites and a high degree of optically induced spin polarization is attainable. When the separation decreases the emission is reduced, the lifetime shortened and the spin polarization downgraded. With separations of <12 A0 there is even no emission. The deterioration occurs as a consequence of electron tunneling in the excited state from NV– to N+ and an optical cycle that involves NV0. The number of pairs with the smaller separations and poorer properties will increase with the number of nitrogen impurities and it follows that the degree of spin polarization that can be achieved for an ensemble of NV− in 1b diamond will be determined and limited by the concentration of single substitutional nitrogen. The information will be invaluable for obtaining optimal conditions when ensembles of NV− are required. As well as extensive measurements of the NV− optical ZPL observations of Stark effects associated with the infrared line at 1042 nm and the optically detected magnetic resonance at 2.87 GHz are also reported.