Etching experiments were performed that reveal the vertical distribution of optically active nitrogen-vacancy (NV) centers in diamond created in close proximity to a surface through ion implantation and annealing. The NV distribution depends strongly on the native nitrogen concentration, and spectral measurements of the neutral and negatively charged NV peaks give evidence for electron depletion effects in lower-nitrogen material. The results are important for potential quantum information and magnetometer devices where NV centers must be created in close proximity to a surface for coupling to optical structures.
The negatively-charged nitrogen-vacancy (NV) center is the most studied optical center in diamond and is very important for applications in quantum information science. Many proposals for integrating NV centers in quantum and sensing applications rely on their tailored fabrication in ultra pure host material. In this study, we use ion implantation to controllably introduce nitrogen into high purity, low nitrogen chemical vapor deposition diamond samples. The properties of the resulting NV centers are studied as a function of implantation temperature, annealing temperature, and implantation fluence. We compare the implanted NV centers with native NV centers present deep in the bulk of the as-grown samples. The results for implanted NV centers are promising but indicate, at this stage, that the deep native NV centers possess overall superior optical properties. In particular, the implanted NV centers obtained after annealing at 2000 °C under a stabilizing pressure of 8 GPa showed an ensemble linewidth of 0.17 nm compared to 0.61 nm after annealing at 1000 °C. Over the same temperature range, the ensemble NV−/NV0 ratio increased by a factor of ∼5, although this was accompanied by an overall decrease in the NV count.
Nitrogen-vacancy (NV) color centers in diamond have emerged as a focal point in quantum technology research due to their exceptional optical and electronic spin properties. This discovery not only expands our understanding of the material properties of diamond but also paves the way for practical applications in quantum technology. As a solid-state spin quantum system characterized by long electron spin coherence times and stable performance, NV color centers offer distinct advantages in quantum information processing. Recent advancements have enabled the fabrication of high-quality NV color centers with controllable concentration and spatial positioning through techniques such as in situ doping, ion implantation, and hybrid approaches. These technological breakthroughs have significantly enhanced the efficiency of NV center fabrication, thereby establishing a robust foundation for their widespread application in quantum sensing and quantum information technologies. This review provides a comprehensive introduction to the structure and fundamental properties of NV color centers in diamond, an in-depth analysis of recent progress in their fabrication techniques, and a critical discussion of their current applications in quantum science and technology. Additionally, the challenges, open questions, and future research directions in NV color center studies are addressed.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.