arXiv:2609.19220

Enhanced Emission and Two-Photon Interference of Lead-Vacancy Centers in Diamond Solid Immersion Lenses

Koyo Hirai, Eiki Ota, Yiyang Chen, Ren Kato, Peng Wang, Toshiharu Makino, Takashi Taniguchi, Masashi Miyakawa, Shinobu Onoda, Mutsuko Hatano, Takayuki Iwasaki

quant-phSubmitted Sep 16, 2026• Announced Sep 17, 2026• 0 citations
arXivHTMLPDF

Abstract

A negatively charged lead-vacancy (PbV-) center in diamond is a novel quantum system which can be operated at a high temperature above 4 K owing to its large ground state splitting. To unlock the quantum properties of the PbV- center, the enhancement of the fluorescence intensity is a key issue. Here, we demonstrate enhanced emission from PbV- centers by a factor of approximately 10 using solid immersion lenses (SILs) fabricated on rough diamond surface caused by high-temperature anneal over 2000°C. Resonant excitation reveals the narrow emission close to the transform-limited linewidth. Furthermore, we demonstrate two-photon interference using one single PbV- center in an SIL. This enhanced emission and indistinguishability will lead to further development of the PbV- center towards quantum network node applications.

Related papers

Transform-Limited Photon Emission from a Lead-Vacancy Center in Diamond above 10 K

Peng Wang, Lev Kazak, Katharina Senkalla +9 more

Transform-limited photon emission from quantum emitters is essential for high-fidelity entanglement generation. In this Letter, we report the coherent optical property of a single negatively charged lead-vacancy (PbV) center in diamond. Photoluminescence excitation measurements reveal stable fluorescence with a linewidth of 39 MHz at 6 K, close to the transform limit estimated from the lifetime measurement. We observe 4 orders of magnitude different linewidths of the two zero-phonon lines, and find that the phonon-induced relaxation in the ground state contributes to this huge difference in the linewidth. Because of the suppressed phonon absorption in the PbV center, we observe nearly transform-limited photon emission up to 16 K, demonstrating its high temperature robustness compared to other color centers in diamond.

arXiv:2308.00995•Physical Review Letters•Feb 15, 2024•25 citations

Two photon interference using a single lead-vacancy center in diamond

E. Ota, K. Hirai, Y.Q.Chen +7 more

The realization of quantum networks is based on the entanglement of stationary qubits via flying photons. Therefore, a fundamental requirement is a single photon source that can efficiently generate indistinguishable photons for the entanglement generation. The group-IV vacancy centers in diamond have emerged as promising candidates due to their spectral stability benefiting from inversion symmetry and long spin coherence time. In particular, the lead-vacancy (PbV) center exhibits fourier-limited linewidths even above 10 K and is predicted to have millisecond-scale spin coherence time near 9 K, making it suitable for scalable quantum networks. Here, we report the indistinguishability of photons emitted from a single PbV center in diamond through a two-photon interference experiment, known as the Hong-Ou-Mandel (HOM) effect. Fluorescence from the PbV center was split into two paths and recombined at a HOM interferometer. Photon correlations were measured for parallel and orthogonal polarized schemes. In parallel polarization, a clear interference dip below 0.5 at zero time delay was observed, whereas for orthogonal polarization, the correlation function exceeded 0.5. These results confirm the generation of indistinguishable photons from a single PbV center, validating their potential as the solid-state quantum emitter. This work paves the way for the PbV-based application for quantum information processing.

•Mar 17, 2026•0 citations

Lead-related quantum emitters in diamond

Matthew E. Trusheim, Noel Wan, Kevin C. Chen +10 more

We report on quantum emission from Pb-related color centers in diamond following ion implantation and high-temperature vacuum annealing. First-principles calculations predict a negatively charged Pb-vacancy (PbV) center in a split-vacancy configuration, with a zero-phonon transition around 2.4 eV. Cryogenic photoluminescence measurements performed on emitters in nanofabricated pillars reveal several transitions, including a prominent doublet near 520 nm. The splitting of this doublet, 5.7 THz, exceeds that reported for other group-IV centers. These observations are consistent with the PbV center, which is expected to have a combination of narrow optical transitions and stable spin states, making it a promising system for quantum network nodes.

arXiv:1805.12202•Physical review. B./Physical review. B•Feb 21, 2019•122 citations

Low-Temperature Spectroscopic Investigation of Lead-Vacancy Centers in Diamond Fabricated by High-Pressure and High-Temperature Treatment

Peng Wang, Takashi Taniguchi, Yoshiyuki Miyamoto +2 more

We report the optical observation of lead-vacancy (PbV) centers in diamond fabricated by Pb ion implantation and subsequent high-temperature annealing (2100 °C) under high pressure (7.7 GPa). Their optical properties were characterized by photoluminescence at varying temperatures down to 5.7 K. We observed intense emission peaks at 550 and 554 nm, with a large splitting of approximately 3900 GHz. The two lines are thought to correspond to the zero phonon line (ZPL) of PbV centers with split ground and excited states. A cubic trend of the ZPL width was observed while varying the temperature. We performed polarization measurements of the two lines in a single PbV center, showing nearly orthogonal dipole polarizations. These optical measurements strongly indicate that the PbV center possesses D 3 d symmetry in the diamond lattice. The observed large ground state splitting significantly suppresses the phonon-mediated transition, which causes decoherence of the electron spin state of the group IV color centers in diamond, leading to the expectation of a long spin coherence time at a temperature ∼9 K.

arXiv:2106.03413•ACS Photonics•Sep 15, 2021•32 citations

Bright Single Lead-Vacancy Center in Diamond Solid Immersion Lens

K. Hirai, Y.Q.Chen, T. Taniguchi +5 more

This study was conducted with the aim of demonstrating the fluorescence enhancement from Pb-V centers in diamond SIL.

•Jul 30, 2025•0 citations

Single-photon emitters based on NIR color centers in diamond coupled with solid immersion lenses

D. Gatto Monticone, J. Forneris, M. Levi +11 more

Single-photon sources represent a key enabling technology in quantum optics, and single color centers in diamond are a promising platform to serve this purpose, due to their high quantum efficiency and photostability at room temperature. The widely studied nitrogen-vacancy (NV) centers are characterized by several limitations, thus other defects have recently been considered, with a specific focus of centers emitting in the near-infra red (NIR). In the present work, we report on the coupling of native NIR-emitting centers in high-quality single-crystal diamond with solid immersion lens (SIL) structures fabricated by focused ion beam (FIB) lithography. The reported improvements in terms of light collection efficiency make the proposed system an ideal platform for the development of single-photon emitters with appealing photophysical and spectral properties.

arXiv:1608.07132•International Journal of Quantum Information•Nov 1, 2014•6 citations
A negatively charged lead-vacancy (PbV-) center in diamond is a novel quantum system which can be operated at a high temperature above 4 K owing to its large ground state splitting. To unlock the quantum properties of the PbV- center, the enhancement of the fluorescence intensity is a key issue. Here, we demonstrate enhanced emission from PbV- centers by a factor of approximately 10 using solid immersion lenses (SILs) fabricated on rough diamond surface caused by high-temperature anneal over 2000°C. Resonant excitation reveals the narrow emission close to the transform-limited linewidth. Furthermore, we demonstrate two-photon interference using one single PbV- center in an SIL. This enhanced emission and indistinguishability will lead to further development of the PbV- center towards quantum network node applications.
Transform-limited photon emission from quantum emitters is essential for high-fidelity entanglement generation. In this Letter, we report the coherent optical property of a single negatively charged lead-vacancy (PbV) center in diamond. Photoluminescence excitation measurements reveal stable fluorescence with a linewidth of 39 MHz at 6 K, close to the transform limit estimated from the lifetime measurement. We observe 4 orders of magnitude different linewidths of the two zero-phonon lines, and find that the phonon-induced relaxation in the ground state contributes to this huge difference in the linewidth. Because of the suppressed phonon absorption in the PbV center, we observe nearly transform-limited photon emission up to 16 K, demonstrating its high temperature robustness compared to other color centers in diamond.
The realization of quantum networks is based on the entanglement of stationary qubits via flying photons. Therefore, a fundamental requirement is a single photon source that can efficiently generate indistinguishable photons for the entanglement generation. The group-IV vacancy centers in diamond have emerged as promising candidates due to their spectral stability benefiting from inversion symmetry and long spin coherence time. In particular, the lead-vacancy (PbV) center exhibits fourier-limited linewidths even above 10 K and is predicted to have millisecond-scale spin coherence time near 9 K, making it suitable for scalable quantum networks. Here, we report the indistinguishability of photons emitted from a single PbV center in diamond through a two-photon interference experiment, known as the Hong-Ou-Mandel (HOM) effect. Fluorescence from the PbV center was split into two paths and recombined at a HOM interferometer. Photon correlations were measured for parallel and orthogonal polarized schemes. In parallel polarization, a clear interference dip below 0.5 at zero time delay was observed, whereas for orthogonal polarization, the correlation function exceeded 0.5. These results confirm the generation of indistinguishable photons from a single PbV center, validating their potential as the solid-state quantum emitter. This work paves the way for the PbV-based application for quantum information processing.
We report on quantum emission from Pb-related color centers in diamond following ion implantation and high-temperature vacuum annealing. First-principles calculations predict a negatively charged Pb-vacancy (PbV) center in a split-vacancy configuration, with a zero-phonon transition around 2.4 eV. Cryogenic photoluminescence measurements performed on emitters in nanofabricated pillars reveal several transitions, including a prominent doublet near 520 nm. The splitting of this doublet, 5.7 THz, exceeds that reported for other group-IV centers. These observations are consistent with the PbV center, which is expected to have a combination of narrow optical transitions and stable spin states, making it a promising system for quantum network nodes.
We report the optical observation of lead-vacancy (PbV) centers in diamond fabricated by Pb ion implantation and subsequent high-temperature annealing (2100 °C) under high pressure (7.7 GPa). Their optical properties were characterized by photoluminescence at varying temperatures down to 5.7 K. We observed intense emission peaks at 550 and 554 nm, with a large splitting of approximately 3900 GHz. The two lines are thought to correspond to the zero phonon line (ZPL) of PbV centers with split ground and excited states. A cubic trend of the ZPL width was observed while varying the temperature. We performed polarization measurements of the two lines in a single PbV center, showing nearly orthogonal dipole polarizations. These optical measurements strongly indicate that the PbV center possesses D 3 d symmetry in the diamond lattice. The observed large ground state splitting significantly suppresses the phonon-mediated transition, which causes decoherence of the electron spin state of the group IV color centers in diamond, leading to the expectation of a long spin coherence time at a temperature ∼9 K.
Single-photon sources represent a key enabling technology in quantum optics, and single color centers in diamond are a promising platform to serve this purpose, due to their high quantum efficiency and photostability at room temperature. The widely studied nitrogen-vacancy (NV) centers are characterized by several limitations, thus other defects have recently been considered, with a specific focus of centers emitting in the near-infra red (NIR). In the present work, we report on the coupling of native NIR-emitting centers in high-quality single-crystal diamond with solid immersion lens (SIL) structures fabricated by focused ion beam (FIB) lithography. The reported improvements in terms of light collection efficiency make the proposed system an ideal platform for the development of single-photon emitters with appealing photophysical and spectral properties.