In this article, we measure the double sideband (DSB) receiver noise temperature (
TrecDSB)of an NbN hot electron bolometer (HEB) mixer at three local oscillator frequencies of 1.6, 2.5, and 5.3 THz. The HEB has cleaned contact interfaces with a 200-nm-thick Au layer. The measured
TrecDSBvalues are 530 ± 11 K, 640 ± 18 K, and 2190 ±150 K at 1.6, 2.5, and 5.3 THz, respectively, using an air setup with total optical losses of 2.60 ± 0.04, 2.63 ± 0.16, and 4.70 ± 0.24 dB, respectively. We derived low mixer noise temperatures (
TmixerDSB)of 240 ± 6 K at 1.6 THz and 290 ± 13 K at 2.5 THz, achieving over 30% improvement compared to published NbN HEB mixers. This enhancement can reduce the integration time of a heterodyne instrument by roughly a factor of 2. At 5.3 THz,
TmixerDSBis 620 ± 55 K, showing limited improvement due to nonoptimized antenna geometry. These results also contribute to understanding the device physics of a wide HEB (4 μm) at high frequencies. The mixer was developed for the proposed Orbiting Astronomical Satellite for Investigating Stellar Systems and Single Aperture Large Telescope for Universe Studies (concept) missions.
NbN hot electron bolometer (HEB) mixers are at this moment the best heterodyne detectors for frequencies above 1 THz. However, the fabrication procedure of these devices is such that the quality of the interface between the NbN superconducting film and the contact structure is not under good control. This results in a contact resistance between the NbN bolometer and the contact pad. We compare identical bolometers, with different NbN - contact pad interfaces, coupled with a spiral antenna. We find that cleaning the NbN interface and adding a thin additional superconductor prior to the gold contact deposition improves the noise temperature and the bandwidth of the HEB mixers with more than a factor of 2. We obtain a DSB noise temperature of 950 K at 2.5 THz and a Gain bandwidth of 5-6 GHz. For use in real receiver systems we design small volume (0.15x1 micron) HEB mixers with a twin slot antenna. We find that these mixers combine good sensitivity (900 K at 1.6 THz) with low LO power requirement, which is 160 - 240 nW at the Si lens of the mixer. This value is larger than expected from the isothermal technique and the known losses in the lens by a factor of 3-3.5.
We report that the heterodyne sensitivity of superconducting hot-electron bolometers (HEBs) increases by 25-30% after annealing at 85degC in high vacuum. The devices studied are twin-slot antenna coupled mixers with a small area NbN bridge of 1 mum times 0.15 mum, above which there is a SiO2passivation layer. The mixer noise temperature, gain, and resistance versus temperature curve of a HEB before and after annealing are compared and analysed. We show that the annealing reduces the intrinsic noise of the mixer by 37% and makes the superconducting transition of the bridge and the contacts sharper. We argue that the reduction ofthe noise is mainly due to the improvement of the transparency of the contact/film interface. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and at a bath temperature of 4.2 K.
We demonstrate that the performance of NbN lattice cooled hot electron bolometer mixers depends strongly on the interface quality between the bolometer and the contact structure. Both the receiver noise temperature and the gain bandwidth can be improved by a factor of 2 by cleaning the interface and adding an additional superconducting interlayer to the contact pad. Using this we obtain a double sideband receiver noise temperature of 950 K at 2.5 THz and 4.3 K, using a 0.4/spl times/4 /spl mu/m HEB mixer with a spiral antenna. At the same bias point, we obtain an IF gain bandwidth of 6 GHz. To comply with current demands on THz mixers for use in space based receivers we reduce the device size to 0.15/spl times/1 /spl mu/m and use a twin slot antenna. We report measurements of the noise temperature, LO power requirement, stability and the direct detection effect, using a mixer with a 1.6 THz twin slot antenna and a 1.462 THz solid state LO source with calibrated output power.
We find that the sensitivity of heterodyne receivers based on superconducting hot-electron bolometer (HEB) increases by 25 − 30% after baking at 85 C and in a high vacuum. The devices studied are twin-slot antenna coupled HEB mixers with a small NbN bridge of 1×0.15 μm. The mixer noise temperature, gain, and resistance versus temperature curve of a HEB before and after baking are compared and analyzed. We show that baking reduces the intrinsic noise of the mixer by 37 % and makes the superconducting transition of the bridge and the contacts sharper. We argue that the reduction of the noise is due to the improvement of the transparency of the contact/film interface. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and a bath temperature of 4.3 K.
To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.