Developing a Chemical and Structural Understanding of the Surface Oxide in a Niobium Superconducting Qubit
Akshay A. Murthy, Paul Masih Das, Stephanie M. Ribet, Cameron Kopas, Jaeyel Lee, Matthew J. Reagor, L.W. Zhou, Matthew Joseph Kramer, Mark C. Hersam, Mattia Checchin, Anna Grassellino, Roberto dos Reis, Vinayak P. Dravid, Alexander Romanenko
Superconducting thin films of niobium have been extensively employed in transmon qubit architectures. Although these architectures have demonstrated improvements in recent years, further improvements in performance through materials engineering will aid in large-scale deployment. Here, we use information retrieved from secondary ion mass spectrometry and electron microscopy to conduct a detailed assessment of the surface oxide that forms in ambient conditions for transmon test qubit devices patterned from a niobium film. We observe that this oxide exhibits a varying stoichiometry with NbO and NbO 2 found closer to the niobium film/oxide interface and Nb 2 O 5 found closer to the surface. In terms of structural analysis, we find that the Nb 2 O 5 region is semicrystalline in nature and exhibits randomly oriented grains on the order of 1–3 nm corresponding to monoclinic N–Nb 2 O 5 that are dispersed throughout an amorphous matrix. Using fluctuation electron microscopy, we are able to map the relative crystallinity in the Nb 2 O 5 region with nanometer spatial resolution. Through this correlative method, we observe that the highly disordered regions are more likely to contain oxygen vacancies and exhibit weaker bonds between the niobium and oxygen atoms. Based on these findings, we expect that oxygen vacancies likely serve as a decoherence mechanism in quantum systems.
Superconducting thin films of niobium have been extensively employed in transmon qubit architectures. Although these architectures have demonstrated improvements in recent years, further improvements in performance through materials engineering will aid in large-scale deployment. Here, we use information retrieved from secondary ion mass spectrometry and electron microscopy to conduct a detailed assessment of the surface oxide that forms in ambient conditions for transmon test qubit devices patterned from a niobium film. We observe that this oxide exhibits a varying stoichiometry with NbO and NbO 2 found closer to the niobium film/oxide interface and Nb 2 O 5 found closer to the surface. In terms of structural analysis, we find that the Nb 2 O 5 region is semicrystalline in nature and exhibits randomly oriented grains on the order of 1–3 nm corresponding to monoclinic N–Nb 2 O 5 that are dispersed throughout an amorphous matrix. Using fluctuation electron microscopy, we are able to map the relative crystallinity in the Nb 2 O 5 region with nanometer spatial resolution. Through this correlative method, we observe that the highly disordered regions are more likely to contain oxygen vacancies and exhibit weaker bonds between the niobium and oxygen atoms. Based on these findings, we expect that oxygen vacancies likely serve as a decoherence mechanism in quantum systems.
High Resolution Image Download MS PowerPoint Slide Improving the qubit’s lifetime (T 1 ) is crucial for fault-tolerant quantum computing. Recent advancements have shown that replacing niobium (Nb) with tantalum (Ta) as the base metal significantly increases T 1, likely due to a less lossy native surface oxide. However, understanding the formation mechanism and nature of both surface oxides is still limited. Using aberration-corrected transmission electron microscopy and electron energy loss spectroscopy, we found that Ta surface oxide has fewer suboxides than Nb oxide. We observed an abrupt oxidation state transition from Ta 2 O 5 to Ta, as opposed to the gradual shift from Nb 2 O 5, NbO 2, and NbO to Nb, consistent with thermodynamic modeling. Additionally, amorphous Ta 2 O 5 exhibits a closer-to-crystalline bonding nature than Nb 2 O 5, potentially hindering H atomic diffusion toward the oxide/metal interface. Finally, we propose a loss mechanism arising from the transition between two states within the distorted octahedron in an amorphous structure, potentially causing two-level system loss. Our findings offer a deeper understanding of the differences between native amorphous Ta and Nb oxides, providing valuable insights for advancing superconducting qubits through surface oxide engineering.
Improving qubit lifetime is essential for fault-tolerant quantum computing. It is widely acknowledged that intricate processing techniques introduce defects at the interfaces and surfaces of superconducting quantum circuits, which can create sources of decoherence. Therefore, a precise understanding of how a material's structure contributes to decoherence is critical for enhancing the performance of superconducting qubits. This talk highlights our recent advancements in understanding surface oxides in resonators and ultrathin aluminum oxide barriers in Josephson junctions (JJs) using transmission electron microscopy and spectroscopy techniques [1-4]. The Superconducting Quantum Materials & Systems Center (SQMS) demonstrated that encapsulating niobium surfaces with a ∼10nm tantalum layer results in 2-5x longer T1 than bare niobium [2]. Our collaborative investigation shows that this improvement is attributed to tantalum's less lossy surface oxide, which contains fewer sub-oxides than niobium oxide. Moreover, the amorphous Ta2O5 shows a bonding nature closer to crystalline form than amorphous Nb2O5, potentially reducing hydrogen diffusion toward the oxide/metal interface [1, 2]. Moreover, we will briefly discuss our preliminary study of the thin film structure under cryogenic conditions down to 20K, conducted using a liquid helium TEM holder in a Thermo Cs-corrected Titan. We also explored the effect of aluminum deposition rates on aluminum oxide microstructure and qubit lifetime. Although increasing the deposition rate from 0.5 Å/s to 5 Å/s significantly improved oxide layer roughness and thickness variation, the qubits’ coherence remained unchanged. This is likely due to Cooper pairs only tunneling through the thinnest parts of the barrier, making them less affected by the grain boundaries in the thin aluminum films. Additionally, we uncovered a stress-induced grain boundary sliding mechanism, which contributes to short-circuit failures in JJs [4]. Our discovery provides vital insight into oxide microstructure and superconducting qubits’ functionality [5].
Superconducting qubits have emerged as a potentially foundational platform technology for addressing complex computational problems deemed intractable with classical computing. Despite recent advances enabling multiqubit designs that exhibit coherence lifetimes on the order of hundreds of μs, material quality and interfacial structures continue to curb device performance. Two-level system defects in the thin superconducting film and adjacent dielectric regions introduce stochastic noise and dissipate electromagnetic energy at the cryogenic operating temperatures. In this study, we utilize time-of-flight secondary ion mass spectrometry to understand the role specific fabrication procedures play in introducing such dissipation mechanisms in these complex systems. We interrogated Nb thin films and transmon qubit structures fabricated through slight modifications in the processing and vacuum conditions. We find that when the Nb film is sputtered onto the Si substrate, oxide and silicide regions are generated at various interfaces. We also observe that impurity species, such as niobium hydrides and carbides, are incorporated within the niobium layer during the subsequent lithographic patterning steps. The formation of these resistive compounds likely impacts the superconducting properties of the Nb thin film. Additionally, we observe the presence of halogen species distributed throughout the patterned thin films. We conclude by hypothesizing the source of such impurities in these structures in an effort to intelligently fabricate superconducting qubits and extend coherence times moving forward.
Qubits made from superconducting materials are a mature platform for quantum information science application, such as quantum computing. However, material-based losses are now a limiting factor in reaching the coherence times needed for applications. In particular, knowledge of the atomistic structure and properties of the circuit materials is needed to identify, understand, and mitigate material-based decoherence channels. In this work, we characterize the atomic structure of the native oxide film formed on Nb resonators by comparing fluctuation electron microscopy experiments to density functional theory calculations, finding that an amorphous layer is consistent with an Nb2O5 stoichiometry. Comparing x-ray absorption measurements at the Oxygen K edge with first-principles calculations, we find evidence of d-type magnetic impurities in our sample, known to cause impedance in proximal superconductors. This work identifies the structural and chemical composition of the oxide layer grown on Nb superconductors and shows that soft x-ray absorption can fingerprint magnetic impurities in these superconducting systems.
Niobium is commonly used for superconducting quantum systems as readout resonators, capacitors, and interconnects. The coherence time of the superconducting qubits is mainly limited by microwave dissipation attributed to two-level system defects at interfaces, such as the Nb/Si and Nb/air interface. One way to improve the Nb/air interface quality is by thermal annealing, as shown by extensive studies in 3D superconducting radio frequency (SRF) cavities. However, it is unclear how the microstructure and chemistry of the interface structures change during heat treatment. To address this knowledge gap, we comprehensively characterized Nb films deposited on Si wafers by physical vapor deposition, including (1) an Nb film from a transmon and (2) an Nb film without any patterning step, using an aberration-corrected transmission electron microscope. Both Nb films exhibit columnar growth with strong [110] textures. There is a double layer between the Nb film and Si substrate, which are amorphous niobium silicides with different Nb and Si concentrations. After in-situ heating of the heterostructure at 360°C inside the microscope, the composition of the double layers at the Nb-Si interface remains almost the same despite different thickness changes. The initial amorphous niobium oxide layer on Nb surface decomposes into face-centered cubic Nb nanograins in the amorphous Nb-O matrix upon heating.
Niobium thin films have been broadly applied in building superconducting qubits for quantum computing hardware. While improvements have been made by device engineering efforts, scaling the energy-sensitive quantum system requires materials study for further improvements. In this study, we performed XPS and ToF-SIMS analysis for Nb thin films across samples with different manufacturing techniques. By varying the air exposure time of the samples, this research comparatively investigates the chemical and depth profile of native oxides before and after the etching process. We observe a rapid logarithmic growth of oxide thickness across all samples and the dominant presence and growth of Niobium pentoxide in atomic percentage concentration on the surface. This comparative study provides insight into oxides mitigation strategies and correlation with qubits performance.