Long-lived sub-levels of the electronic ground-state manifold of rare-earth ions in crystals can be used as atomic population reservoirs for photon echo-based quantum memories. We measure the dynamics of the Zeeman sub-levels of erbium ions that are doped into a lithium niobate waveguide, finding population lifetimes at cryogenic temperatures down to 0.7 K as long as seconds. Then, using these levels, we prepare and characterize atomic frequency combs (AFCs), which can serve as a memory for quantum light at 1532 nm wavelength. The results allow predicting a 0.1% memory efficiency, limited mainly by unwanted background absorption that we believe to be caused by excitation-induced erbium spin flips and frequency shifting due to two-level systems or non-equilibrium phonons. Hence, while it should be possible to create an AFC-based quantum memory in E r 3 + : T i 4 + : L i N b O 3 , improved crystal growth together with optimized AFC preparation will be required to make it suitable for applications in quantum communication.
Long-lived sub-levels of the electronic ground-state manifold of rare-earth ions in crystals can be used as atomic population reservoirs for photon echo-based quantum memories. We measure the dynamics of the Zeeman sub-levels of erbium ions that are doped into a lithium niobate waveguide, finding population lifetimes at cryogenic temperatures down to 0.7 K as long as seconds. Then, using these levels, we prepare and characterize atomic frequency combs (AFCs), which can serve as a memory for quantum light at 1532 nm wavelength. The results allow predicting a 0.1% memory efficiency, limited mainly by unwanted background absorption that we believe to be caused by excitation-induced erbium spin flips and frequency shifting due to two-level systems or non-equilibrium phonons. Hence, while it should be possible to create an AFC-based quantum memory in E r 3 + : T i 4 + : L i N b O 3 , improved crystal growth together with optimized AFC preparation will be required to make it suitable for applications in quantum communication.
This thesis describes experiments aimed at developing a key component in applications such as quantum networks and long-distance quantum communication systems: quantum memories. Quantum memories for light using photon-echo and coherent rephrasing techniques have been developed. The work is carried out on rare-earth-ion-doped inorganic crystals. Several properties are associated with these crystals such as long coherence times and long-lived ground state sublevels that are particularly interesting in connection applications in the area of quantum information science. It is demonstrated the preparation of optical inhomogeneous absorption profiles such that the light only interacts with a specific transition at a selected frequency. Narrow absorbing structures with widths of <100 kHz have been prepared with no absorption in the surrounding spectral interval. Most of the experiments were carried out using Pr3+:Y2SiO5. However, in our search for suitable a Λ-system in the material under consideration, we also performed spectral hole-burning spectroscopy in Nd:Y2SiVO4. As part of the search for host materials for Pr, Pr:La2(WO4)3 crystal was characterized using a variety of methods, such as, hole burning and photon-echoes. Electromagnetically induced transparency was also observed in this crystal. The most important criteria for evaluating quantum memory performance and the most important physical requirements are discussed. After investigating the standard photon echo techniques and controlled reversible inhomogeneous broadening (CRIB) for quantum state storage, we considered an efficient multimode quantum memory protocol; the atomic frequency comb (AFC) protocol. Combs with peaks of widths 100-300 kHz and an optical depth of~ 10 were created by optical pumping inside an emptied region of the inhomogeneous profile of Pr3+:Y2SiO5, allowing us to improve the efficiency of light storage. Light storage combining a photon-echo technique based on an AFC and spin-wave storage have been demonstrated, and an experimental AFC scheme for the storage of weak coherent light pulses in Pr3+:Y2SiO5 is presented. Finally, we have investigated superradiance and slow light effects. Both these effects occur in the high optical depth regime and can influence the memory performance. Under certain conditions superradiance results in the immediate re-emission of the stored light in a single burst of coherent radiation, and inside spectrally structured materials, slow light effects may result when storage is performed.
Quantum memories are a key building block for optical quantum computers and quantum networks. Rare-earth ion-doped crystals are a promising material to achieve quantum memory using an atomic frequency comb protocol. However, current atomic frequency comb memories typically use bulk materials or waveguides with large cross sections or rely on fabrication techniques not easily adaptable to wafer scale processing. Here, we demonstrate a compact chip-integrated atomic frequency comb in rare-earth-doped thin-film lithium niobate. Our optical memory exhibits a broad storage bandwidth exceeding 100 MHz and optical storage time as long as 250 ns. The enhanced optical confinement in this device leads to three orders of magnitude reduction in optical power required for a coherent control as compared to ion-diffused waveguides. These compact atomic frequency comb memories pave the way toward scalable, highly efficient, electro-optically tunable quantum photonic systems that can store and manipulate light on a compact chip.
When doped into solid state transparent crystals, rare-earth ions can have optically excited states with milliseconds coherence time and up to six hours coherence time for hyperfine levels after being cooled down to liquid helium temperature. This long coherence property makes them unique as solid state material and attractive for quantum information applications.The rare-earth ions have narrow homogeneous linewidths on the order of ~ kHz. When doped into a crystal, the lattice structure is slightly distorted due to the size mismatch between the dopant and the host ions, resulting in slight differences in the local crystal fields at the dopant sites. Therefore, the resonance frequencies of the rare-earth ions are shifted relatively, resulting in an inhomogeneously broadened absorption profile, typically on the order of a few GHz. This provides the possibility of addressing each group of ions individually and engineering the absorption profile for different purposes by optical pumping using a narrow linewidth laser, and makes rare-earth-ion-doped crystals suitable for ensemble based quantum memories.Quantum memories are vital components for developing longdistance quantum communication. Part of this thesis project focused on making quantum memories with high efficiency and long storage time, especially using materials with low optical depth. To achieve this goal, a low finesse, unsymmetrical cavity was employed and experiments were carried out at (or close to) the impedance matched condition. Atomic frequency comb (AFC) protocol proposed for such an inhomogeneously broadened system was used to store coherent light for a certain time. 56% overall efficiency was achieved, and the main limiting factor for reaching even higher efficiency was the inefficient coupling between incoming light and the cavity mode. Other possible loss mechanisms were analyzed as well.Long-time, on-demand, quantum memory experiments were conducted with the help of two efficient radio-frequency rephasing pulses. Storage time was extended from microseconds to milliseconds after compensating (most of) the residual earth magnetic field in the lab. The opportunities and challenges of combing the cavity assistant quantum memory and the long time, on demand quantum memory were analyzed and possible solutions were proposed. Another part of the thesis project involves slow light-based applications in rare-earth-ion-doped crystals. The strong slow light effect at the presence a spectral hole is due to the fact that the light interacts with the absorbing ions outside the spectral hole off-resonantly, and most of the light energy is stored inside the ions as a polarization. For example, with a group velocity of 300 km/s, 99.9% of the pulse energy is stored in the ions when the pulse propagates inside the crystal. The slower the light propagates, the more energy is stored inside the medium. Based on this, a frequency shifter that is capable of shifting the light frequency of ± 4 MHz was demonstrated, and frequency shift up to GHz was proposed. Group velocity control by a factor of 20 and pulse compression in time by a factor of 2 were also demonstrated. The frequency shift and group velocity of the light are solely controlled by the external electric field, which makes them ideal for weak light situation. The unique property of such a frequency shifter and group velocity controller is that they could be made to accept light from an arbitrary incoming angle and polarization, for example, scattered light.
Quantum memories are used for storing the quantum mechanical states of photons and release identical photons at a later time. This has many applications within the field of quantum computing and is also essential in order to achieve long range quantum communication and cryptography. In this thesis Atomic frequency comb (AFC) quantum memories were investigated. In particular, three-level memory schemes were investigated in detail and a program for simulating these protocols was developed. These schemes make use of control pulses to transfer the population from the optically excited state to a ground state hyperfine level, as well as radio frequency fields to swap the population in the two ground state hyperfine levels. In this work control and RF pulses, tailored to give good transfer rates, are suggested and effects due to off resonant excitation was investigated. A memory protocol which could give efficiencies up to 60% for Praseodymium doped Yttrium Silicate based AFC memories is proposed. The main bottleneck for reaching higher efficiencies is that the AFC peak spacing needs to be small in order to give enough time to transfer the population to the spin state with the control pulses. With the control pulses suggested in this work and the current technology of tailoring AFC peaks in Pr-based memories, this gives a maximum finesse of 6 of the AFC structure.
Optical quantum memories will enable technologies including long distance quantum communication and modular quantum computing. Rare earth ion doped crystals provide an excellent solid state platform for optical quantum memories. Among rare earths, erbium is particularly appealing due to its long-lived telecom-wavelength resonance, allowing integration with silicon photonics and with existing optical communication technology and infrastructure. We present an on-chip all-optical quantum memory at telecom wavelengths using a nanobeam photonic crystal cavity fabricated directly in erbium-167 doped yttrium orthosilicate. Using an atomic frequency comb protocol, we store coherent pulses for memory times as long as 10 µs, albeit with low efficiency. For shorter memory times, we achieve a memory efficiency of 0.4%, which is limited by the coupling rate between the resonator and the ensemble of ions. By working at dilution refrigerator temperatures, we are able to access a regime where the ions have long optical coherence times and good spectral holeburning properties using only a moderate magnetic field applied with permanent magnets. We characterize the multimode properties and fidelity of the quantum memory in this device, and outline a path toward higher efficiency.
A long-lived quantum memory is a firm requirement for implementing a quantum repeater scheme. Recent progress in solid-state rare-earth-ion-doped systems justifies their status as very strong candidates for such systems. Nonetheless an optical memory based on spin-wave storage at the single-photon level has not been shown in such a system to date, which is crucial for achieving the long storage times required for quantum repeaters. In this paper we show that it is possible to execute a complete atomic frequency comb (AFC) scheme, including spin-wave storage, with weak coherent pulses of $\overline{n}=2.5\ifmmode\pm\else\textpm\fi{}0.6$ photons per pulse. We discuss in detail the experimental steps required to obtain this result and demonstrate the coherence of a stored time-bin pulse. We show a noise level of $(7.1\ifmmode\pm\else\textpm\fi{}2.3)\ifmmode\times\else\texttimes\fi{}{10}^{\ensuremath{-}3}$ photons per mode during storage, and this relatively low noise level paves the way for future quantum optics experiments using spin waves in rare-earth-doped crystals.