Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.
Abstract The nitrogen-vacancy (NV) center in diamond is a promising quantum system for magnetometry applications exhibiting optical readout of minute energy shifts in its spin sub-levels. Key material requirements for NV ensembles are a high NV − concentration, a long spin coherence time and a stable charge state. However, these are interdependent and can be difficult to optimize during diamond growth and subsequent NV creation. In this work, we systematically investigate the NV center formation and properties in bulk chemical vapor deposition (CVD) diamond. The nitrogen flow during growth is varied by over four orders of magnitude, resulting in a broad range of single substitutional nitrogen concentrations of 0.2–20 parts per million. For a fixed nitrogen concentration, we optimize electron-irradiation fluences with two different accelerated electron energies, and we study defect formation via optical characterizations. We discuss a general approach to determine the optimal irradiation conditions, for which an enhanced NV concentration and an optimum of NV charge states can both be satisfied. We achieve spin–spin coherence times T 2 ranging from 45.5 to 549 μ s for CVD diamonds containing 168 to 1 parts per billion NV − centers, respectively. This study shows a pathway to engineer properties of NV-doped CVD diamonds for improved sensitivity.
We systematically investigate the NV center creation and properties in bulk chemical vapor deposition (CVD) diamond, throughout growth, electron-beam irradiation, and annealing steps. We study diamond series grown with a varying nitrogen flow over 4 orders of magnitude, resulting in a broad range of single substitutional nitrogen (P1 center) densities from 0.2 to 20 ppm. We investigate in-situ P1 and NV creations, as well as NV charge states distributions. As the next step, we optimize electron-irradiation fluences for a fixed nitrogen concentration, with two different accelerated electron energies. We bring up a general approach to determine the optimal irradiation conditions, and discuss criteria for P1 to NV conversion ratios in the context of stable NV charge states. Through all these optimizations, we enhance the NV- concentration remarkably in our CVD diamond samples, without sacrificing their Hahn-echo coherence time T2. We achieve NV concentrations from 1 to 168 ppb with T2 from 549 to 45.5 µs respectively. This study shows a pathway to engineer targeted, optimized properties of NV-ensembles in bulk CVD diamonds for improved sensitivity.
The Nitrogen-Vacancy (NV) color center is a defect of diamond which behaves as an artificial atom hosted in a solid-state matrix. Due to its electron spin properties which can be read-out and manipulated as an elementary quantum system, the NV center has found a wide panel of applications as a qubit for quantum information and as a magnetic field sensor. However these applications require to control the properties of the NV centers and their localization. This doctoral thesis investigates methods allowing us to tailor the properties of NV centers by combining techniques for the implantation of nitrogen atoms and the plasma-assisted (CVD) synthesis of diamond.The manuscript is divided into six chapters. The first chapter summarizes the properties of the NV center which will set our objectives for the NV engineering. The second chapter will describe how arrays of NV centers can be created using Focused Ion Beam implantation. The results open a wide range of applications for the targeted creation of NV centers in diamond structures such as photonic crystals and tips. However the low kinetic energy which is required for achieving implantation within a spot of 10-nm diameter leads to shallow defects which properties are strongly affected by the sample surface. The third chapter investigates how the overgrowth of a diamond layer over implanted NV centers can remove the detrimental influence of the surface. The fourth and fifth chapters describe effective methods for NV center fabrication through the control of the CVD growth conditions of the hosting crystal. Thin layers with high NV doping can be grown and almost perfect control of the orientation of the NV axis can be achieved. With the goal to optimize the spin coherence properties, the sixth chapter investigates how the electron spin of the NV center can be protected from decoherence effects induced by magnetic noise due to the unpolarized spins in the diamond lattice.
The negatively-charged nitrogen-vacancy (NV) center is the most studied optical center in diamond and is very important for applications in quantum information science. Many proposals for integrating NV centers in quantum and sensing applications rely on their tailored fabrication in ultra pure host material. In this study, we use ion implantation to controllably introduce nitrogen into high purity, low nitrogen chemical vapor deposition diamond samples. The properties of the resulting NV centers are studied as a function of implantation temperature, annealing temperature, and implantation fluence. We compare the implanted NV centers with native NV centers present deep in the bulk of the as-grown samples. The results for implanted NV centers are promising but indicate, at this stage, that the deep native NV centers possess overall superior optical properties. In particular, the implanted NV centers obtained after annealing at 2000 °C under a stabilizing pressure of 8 GPa showed an ensemble linewidth of 0.17 nm compared to 0.61 nm after annealing at 1000 °C. Over the same temperature range, the ensemble NV−/NV0 ratio increased by a factor of ∼5, although this was accompanied by an overall decrease in the NV count.
Precise control over the spatial distribution and charge state of nitrogen-vacancy (NV) centers in diamond is a key requirement for further advancing this platform in quantum sensing and photonic applications. Here, we investigate nitrogen ion implantation as a scalable method to engineer NV centers in bulk single-crystalline (SC) and a 5 μ m -thick polycrystalline (PC) diamond membrane. Nitrogen-doped regions (1–80 ppm) were fabricated using a 0.7 MeV ion beam and high-temperature annealing, with NV center formation verified by confocal fluorescence imaging and spectral analysis. In SC bulk diamond, we estimate the NV concentration from spectral analysis and model the fluorescence response as a function of implantation dose, capturing both the initial increase at low concentrations and a saturation behavior at higher doses due to quenching mechanisms. In contrast, PC diamond membranes show a weaker dependence at low implantation fluences, consistent with pre-existing nitrogen impurities, thus making a statistical model significantly more complex. The activation yield is found to be of order of 1%, which is lower than in N-rich diamond samples, as implanted N is predominantly interstitial. Photoluminescence spectroscopy indicates that NV 0 is the dominant charge state in both materials, with a laser-power-dependent redistribution between neutral and negative charge states. Optically detected magnetic resonance (ODMR) measurements in SC bulk diamond resolve the hyperfine structure and allow extraction of the dephasing time ( T 2 ∗ ), while in PC diamond membranes, where NV centers tend do form near the grain boundaries, the ODMR signals are observed but spectral resolution is currently limited by impurities, grain-dependent NV orientations, and photoluminescence background.